Abstract:Concrete facilities in the severe-cold areas of western China (salt lake environments and heavy saline soils) are seriously damaged by the multiple corrosion effects of freeze–thaw cycles and sulfate corrosion. Magnesium phosphate cement (MPC) cement-based material has become an ideal concrete structural component because of its superior performance. Because concrete structural repair materials are used in heavy-corrosion environments, their durability in those environments should also be considered. Regarding the salt-freezing resistance of MPC, the existing studies have all used a NaCl solution as the heat transfer medium. In addition to chlorine salt, sulfate, especially Na2SO4, is also common in typical use environments such as oceans, salt lakes, and groundwater. To evaluate the sulfate freeze–thaw resistance of potassium magnesium phosphate cement (MKPC) mortar, in this study the strength development, weight loss, and water absorption of MKPC mortar specimens subjected to different freeze–thaw cycles were tested and compared with those for Portland cement (P.O) mortar specimens of the same strength grade. The results showed that the P.O mortar specimen completely lost its strength after 75 cycles of rapid water freezing and thawing and 50 cycles of sodium sulfate solution (5%) freezing and thawing. However, the residual strength rating of the MKPC mortar specimen after 75 cycles of water freezing and thawing and 100 cycles of sodium sulfate solution freezing and thawing was higher than 75%. After 50 rapid freeze–thaw cycles in water and a 5% Na2SO4 solution, the P.O mortar specimen’s mass loss exceeded the 5% failure standard, whereas the mass loss of the MKPC mortar specimens was much less than 5%. Before the freeze–thaw cycles, the water absorption of the P.O mortar specimen was close to 8 times that of the MKPC mortar specimen, and after 50 water freeze–thaw cycles and 25 sulfate solution freeze–thaw cycles, the water absorption reached 4.88% and 5.68%, respectively. However, after 225 freeze–thaw cycles in water and the sulfate solution, the water absorption rates of MKPC mortar specimens were 2.91% and 2.51% respectively. The test and analysis results show that the freeze–thaw resistance of MKPC mortar was much higher than that of Portland cement mortar specimens. Those results provide a prerequisite for applying and expanding the use of MKPC-based materials in severe-cold areas of western China (salt lake and heavily saline soil environments).

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

Compositional Dependence of Pore Structure, Strengthand Freezing-Thawing Resistance of Metakaolin-Based Geopolymers

Early-Stage Geopolymerization Process of Metakaolin-Based Geopolymer

Study on the Chloride–Sulfate Resistance of a Metakaolin-Based Geopolymer Mortar

The influence of Si/Al ratio on sulfate durability of metakaolin-based geopolymer

Sulfate Resistance and Microstructure of Metakaolin Geopolymer Reinforced by Cellulose Nanofiber and Wollastonite

Deterioration of alkali-activated and Portland cement-based mortars under sulfur oxidizing bacteria corrosion

Durability Performances of Wollastonite, Tremolite and Basalt Fiber-Reinforced Metakaolin Geopolymer Composites under Sulfate and Chloride Attack

Durability study and mechanism analysis of red mud-coal metakaolin geopolymer concrete under a sulfate environment

Multiscale Study of Sodium Sulfate Soaking Durability of Low Plastic Clay Stabilized by Reactive Magnesia-Activated Ground Granulated Blast-Furnace Slag

Study on the Stability of Low-Carbon Magnesium Cementitious Materials in Sulfate Erosion Environments

Calcium-Free Geopolymer As A Stabilizer for Sulfate-Rich Soils

Metakaolin Based Geopolymer Mortar As Concrete Repairs: Bond Strength and Degradation when Subjected to Aggressive Environments

Contradict mechanism of long-term magnesium and sodium sulfate attacks of nano silica-modified cement mortars – Experimental and thermodynamic modeling

Understanding the Influence of Compressive Strength, Microstructure, and Mechanism for Metakaolin-Based Geopolymer under Varying Rest Periods in the Curing Process

Durability of Magnesium Potassium Phosphate Cements (MKPCs) under Chemical Attack

Effect and evaluation of multi-factors on the performance of one-part geopolymer mortar against MgSO 4 erosion

Sulfate Freeze–Thaw Resistance of Magnesium Potassium Phosphate Cement Mortar

Mechanical Strength and the Degradation Mechanism of Metakaolin Based Geopolymer Mixed with Ordinary Portland Cement and Cured at High Temperature and High Relative Humidity

Sulfate resistance of hybrid fiber reinforced metakaolin geopolymer composites

Stabilization soft Clay Soil using Metakaolin based Geopolymer