Abstract:Sulfate resistance of high-volume fly ash/cement mortars hybrid containing 0~1.5 wt.% of nano-silica (Nano-SiO2, NS) and 0~1.0 vol.% of polyvinyl alcohol (PVA) fibers was investigated in this study. Fly ash was replaced with Portland cement at levels of 60% by weight. The resistance to sulfate attack was investigated by exposing the mortars to 10 wt.% sodium sulfate (Na2SO4) solutions for 72 days, after which change in mass, compressive, and flexural strengths were determined. For comparison, the compressive and flexural strengths of cement mortar after 100 days of curing in water were also investigated. Microstructural deteriorations caused by sulfate attack were analyzed by using scanning electron microscope (SEM). The test results showed that the combination of NS and PVA fibers was effective in enhancing the mechanical properties and the resistance to sulfate attack. After 28 days curing, the hybrid addition of 1.5 wt.% NS and 1.0 vol.% PVA fibers increased the flexural strength by 90% over the control one without NS and PVA fiber. Moreover, regardless of PVA fibers content, due to the crystal nucleus and pore-filling effects, the adding of 0.5 wt.% NS increased the compressive strength by 67.1~118.2%. Chemical reaction took place between fly ash and Na2SO4 as no un-hydration particles could be observed in the samples immersed in Na2SO4 solutions for 72 days, while a lot of un-hydration fly ash particles could be found in the SEM image of mortar after 100 days curing in water. The chemical reaction production could increase the adhesive property and fill the pores of cement mortar. As a result, the compressive and flexural strengths of cement mortars after immersed in Na2SO4 solution for 72 days, were much higher than that after 28 days curing. Moreover, the compressive strength of mortars incorporating 1.0~1.5 wt.% NS was even higher than that after 100 days curing in water, indicating the combination of Nano-SiO2/PVA fiber is effective in enhancing the resistance to sulfate attack.

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Influence of Super Absorbent Polymer on the Sulfate Resistance of Cement Mortar

Roles of fly ash, granulated blast-furnace slag, and silica fume in long-term resistance to external sulfate attacks at atmospheric temperature

Effect of Seawater on Hydration and Sulfate Resistance of Noncement Mortars

Sulfate resistance and hydration products of steam cured steel slag blended cement mortar under dry–wet cycle

Deterioration of Mortar Bars Using Binary and Ternary Mixtures Immersed in Sodium Sulfate Solutions

Effect of steel slag powder, fly ash, and silica fume on the mechanical properties and durability of cement mortar

Effect of internal sulfate attack on the properties of sulfate-resisting cement and alkali-activated slag

Durability self-compacting mortar under external chemical attacks based on composite binder

Effect of Different Mineral Admixtures on Sulfate Attack to Mortars

The Influence of External Sulfate Attack on the Durability of Reinforced Mortars in the Presence of Calcined River Sediments

Effect of mineral admixtures on the resistance to sulfate attack of reactive powder concrete

Evaluation of the early strength of limestone-slag-cement ternary composite mortar improved by aluminum sulfate

Effect of Mineral Admixtures on Physical, Mechanical, and Microstructural Properties of Flue Gas Desulfurization Gypsum-Based Self-Leveling Mortar

Effect of Nano-SiO2/PVA Fiber on Sulfate Resistance of Cement Mortar Containing High-Volume Fly Ash

Durability of phosphogypsum-based supersulfated cement mortar against external attack by sodium and magnesium sulfate

Mechanical and Durability Properties of Mortars Incorporating Red Mud, Ground Granulated Blast Furnace Slag, and Electric Arc Furnace Dust

Study on the Chloride–Sulfate Resistance of a Metakaolin-Based Geopolymer Mortar

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles