Abstract:This study assessed the impact of calcium silicate slag (CSS), an industrial by-product of aluminum extraction from fly ash, on the reaction kinetics, compressive strength, and efflorescence of one-part sodium carbonate-activated slag (SCS). Various proportions of CSS (0%, 10%, and 20%) were used to substitute for slag. The resulting performances were evaluated through chemical shrinkage, heat liberation, compressive strength, water absorption, phase composition (XRD and TG.), microstructures (BET and BSE-EDS), and simulated efflorescence test (partially and fully immersed in deionized water). The results indicate that the CSS possesses a porous structure. The addition of CSS impairs flowability but accelerates the development of chemical shrinkage and heat liberation. The incorporation of CSS promotes the transformation of gaylussite, leading to an increase in CASH and hydrotalcite formation. Consequently, a higher compressive strength and a lower water adsorption rate are achieved. 10% CSS addition improves the splitting tensile strength of SCS under conditions of partial immersion in the efflorescence test. However, a 20% CSS substitution exacerbates the formation of efflorescence products and reduces the splitting tensile strength. These observations are associated with residual alkalis in CSS, a lower Al/Si ratio of products, and an increase in capillary pores attributed to CSS particles. This paper demonstrates the feasibility of using alkaline solid waste for slag substitution and performance regulation in SCS and reveals the underlying mechanism. The prepared CSS-SCS binder exhibits much lower energy consumption and CO2 emission than traditional cement-based material, as determined by life cycle assessment.

Durability of phosphogypsum-based supersulfated cement mortar against external attack by sodium and magnesium sulfate

Resistance of phosphogypsum-based supersulfated cement to carbonation and chloride ingress

Early-age carbonation mitigation of SSC by CxS minerals: Mechanism and Performances

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

MgO-based supersulfated cement with different industrial by-product gypsum: Experiments and molecular dynamics simulation

The mechanical properties of supersulphated cement containing phosphogypsum

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

Mechanical properties and hydration mechanism of super-sulfated cement prepared with ordinary Portland cement, carbide slag, and sodium silicate

Hydration behavior and strength development of supersulfated cement prepared by calcined phosphogypsum and slaked lime

Contradict mechanism of long-term magnesium and sodium sulfate attacks of nano silica-modified cement mortars – Experimental and thermodynamic modeling

Role of supplementary cementing materials on reducing damage due to internal sulphate attack in concrete

Evaluation of Sulfate Resistance of Calcined Dolomite Activated Ground Granulated Blast Furnace Slag

An Eco-Friendly Phosphogypsum-Based Cementitious Material: Performance Optimization and Enhancing Mechanisms

Roles of fly ash, granulated blast-furnace slag, and silica fume in long-term resistance to external sulfate attacks at atmospheric temperature

Effect of modified phosphogypsum on the hydration properties of the phosphogypsum-based supersulfated cement

Study on the Chloride–Sulfate Resistance of a Metakaolin-Based Geopolymer Mortar

Durability self-compacting mortar under external chemical attacks based on composite binder

Mitigation potential of sulfate-resistant Portland cement for internal sulfate attack

Application of various microscopy techniques to study early‐age and longer‐term behaviour of super sulphated cement microstructure