Abstract:Extensive research has been conducted on the sulfate attack of concrete structures; however, the need to adopt the use of more sustainable materials is driving a need for a quicker test method to assess sulfate resistance. This work presents accelerated methods that can reduce the time required for assessing the sulfate resistance of mixtures by 70%. Class F fly ash has historically been used in concrete mixtures to improve sulfate resistance. However, environmental considerations and the evolving energy industry have decreased its availability, requiring the identification of economically viable and environmentally friendly alternatives to fly ash. Another challenge in addressing sulfate attack durability issues in concrete is that the standard sulfate attack test (ASTM C1012) is time-consuming and designed for only standard mortars (not concrete mixtures). To expedite the testing process, accelerated testing methods for both mortar and concrete mixtures were adopted from previous work to further the development of the accelerated tests and to assess the feasibility of testing the sulfate resistance of mortar and concrete mixtures rapidly. This study also established criteria for interpreting sulfate resistance for each of the test methods used in this work. A total of 14 mortar mixtures and four concrete mixtures using two types of Portland cement (Type I and Type I/II) and various supplementary cementitious materials (SCMs) were evaluated in this study. The accelerated testing methods significantly reduced the evaluation time from 12 months to 21 days for mortar mixtures and from 6 months to 56 days for concrete mixtures. The proposed interpretation method for mortar accelerated test results showed acceptable consistency with the ACI 318-19 interpretations for ASTM C1012 results. The interpretation methods proposed for the two concrete sulfate attack tests demonstrated excellent consistency with the ASTM C1012 results from mortar mixtures with the same cementitious materials combinations. Metakaolin was shown to improve sulfate resistance for both mortar and concrete mixtures, while silica fume and natural pozzolan had a limited impact. Using 15% metakaolin in mortar or concrete mixtures with Type I/II cement provided the best sulfate resistance.

Mitigation potential of sulfate-resistant Portland cement for internal sulfate attack

Combined effect of alkali-aggregate reaction (AAR) and internal sulfate attack (ISA): Microstructural and porous structure modifications of portland cement mortars

Influence of internal sulfate attack on cement paste properties: contamination by pyrite

Effect of Exposure Conditions on Mortar Subjected to an External Sulfate Attack

Sulfate attack on concrete with mineral admixtures

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Durability of phosphogypsum-based supersulfated cement mortar against external attack by sodium and magnesium sulfate

Internal sulfate attack in mortars containing contaminated fine recycled concrete aggregates

Effect of external sulfate attack on the tensile properties of fiber-reinforced sprayed concrete

Rapid Assessment of Sulfate Resistance in Mortar and Concrete

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Influence of accelerator type and dosage on the durability of wet-mixed sprayed concrete against external sulfate attack

Roles of fly ash, granulated blast-furnace slag, and silica fume in long-term resistance to external sulfate attacks at atmospheric temperature

Effect of self-healing in closing cracks from the sulfate attack in Portland, supersulfated and alkali-activated cement

Deterioration of Mortar Bars Using Binary and Ternary Mixtures Immersed in Sodium Sulfate Solutions

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Ultrasonic and impact spectroscopy monitoring on internal sulphate attack of cement-based materials

Influence of Ca2+ on Early Degradation of Cast-In-Situ Mortar Induced by Sulfate-Magnesium Multiple Combined Attack

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Effect of sulfate attack on multiple interfacial transition zones of high-belite sulfoaluminate cement recycled concrete