Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Gaozhan Zhang,Cong Wu,Dongshuai Hou,Jun Yang,Daosheng Sun,Xiaojia Zhang

DOI: https://doi.org/10.1016/j.compositesb.2021.108862

2021-07-01

Abstract:<p>The degradation of material induced by sulfate attack is major durability problem facing cementitious materials. In this paper, to illustrate the nanoscale chemical degradation, Portland cement samples were exposed to 5wt.% NaSO₄ solution with different pH values (pH = 13, 8 and 5) as the function of corrosion ages (28 and 180 days). The effects of pH value on the hydrate phase, morphology and microstructure of cement hydration products under sulfate attack were characterized in combination with XRD, SEM-EDS, ¹H, ²⁷Al and ²⁹Si NMR. The results demonstrate that reducing pH value of sulfate solution facilitates the formation and precipitation of columnar and platelet gypsum crystals in cement paste, whereas inhibiting the ettringite formation. A slight increase in the proportion of deleterious micropores larger than 1.6 μm as the sample exposed to sulfate with low pH value. The ettringite induced by sulfate attacking is transformed to AFm at early period and reversal transformation happens at later period. Reduction of the pH value of sulfate solution accelerates the transformation reaction of the hexa-coordinated aluminate phases. ²⁹Si NMR test revealed that with pH reducing from 13 to 5, the hydration degree increase nearly 18%, the mean silicate chain length increase by 66.2% and Al[4]/Si ratio increase by nearly 30%. Also, the silicate polymerization enhancement is closely related with Al³⁺ ions extraction at early sulfate-attack period and re-entering at late sulfate-attack period. This research might provide nanoscale insights to guide more durable cement-based material in detrimental environment.</p>

engineering, multidisciplinary,materials science, composites

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the influence of different pH values on the phase composition and microstructure of cement paste in a sulfate - erosion environment. Specifically, the research aims to explore how pH values affect the chemical degradation process of cement hydration products under sulfate attack, especially the specific effects on the hydration phase, morphology and microstructure. Through this research, the author hopes to provide nano - scale insights and technical guidance for the preparation of more durable cement - based materials in a harmful environment.

In the study, the author used a variety of technical means such as X - ray diffraction (XRD), scanning electron microscope (SEM - EDS), 1H nuclear magnetic resonance (NMR), 27Al NMR and 29Si NMR to characterize the phase composition, micromorphology and pore characteristics of Portland cement samples after 28 days and 180 days of corrosion at different pH values (pH = 13, 8, 5). The experimental results show that reducing the pH value of the sulfate solution promotes the formation and precipitation of columnar and plate - like gypsum crystals, inhibits the formation of ettringite, and as the pH value decreases, the proportion of harmful micropores (greater than 1.6 μm) increases slightly. In addition, the study also found that the decrease in pH value accelerates the conversion reaction of the six - coordinated aluminate phase. The 29Si NMR test shows that when the pH value drops from 13 to 5, the degree of hydration increases by nearly 18%, the average silicate chain length increases by 66.2%, and the Al[4]/Si ratio increases by nearly 30%. These findings are of great significance for understanding the microstructure changes and durability of cement - based materials under sulfate attack.