Abstract:This study investigated the effect of layered double hydroxides (LDHs) on the deterioration process of cement paste in the sulfate environment. Cement pastes with the addition of original and calcined LDHs at 2.5 wt.% and 5.0 wt.% of cement were exposed to Na2SO4 solution for 360 days. The macroscopic performance of the cement paste was assessed based on mass variation, porosity, compressive strength, and content of sulfate ions. Furthermore, the microhardness, microstructures, and composition of the degraded pastes were examined using Vickers hardness (HV), mercury intrusion porosimetry (MIP), scanning electron microscope (SEM), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The results indicate that cement paste incorporated with LDHs can mitigate the corrosion caused by sulfate effectively, especially in the case of calcined LDHs (C-LDHs), which primarily increase the adsorption of sulfate. Compared with the control specimen, the 180 d compressive strength loss ratio of specimens with 2.5 wt.% and 5.0 wt.% of C-LDHs decreased by 63.66% and 80.51%, respectively. Moreover, LDHs can reduce the amount of ettringite crystals, densify the microstructure, and refine the pore structure to mitigate the cement paste's sulfate corrosion significantly. Compared with the control specimen, the 180 d harmful pore volume fraction of specimens laced with 2.5 wt.% and 5.0 wt.% C-LDHs decreased by 43.77% and 54.51%, respectively. In terms of the content of C-LDHs, an optimal content of C-LDHs could ensure the dominant effect of adsorption, while excessive C-LDHs could refine pores. In addition, Vickers hardness has an excellent correlation with compressive strength, which could precisely predict the compressive strength. Moreover, by combining the Vickers hardness distribution and content distribution of sulfate ions, the cross-section of the paste could be classified into four regions to evaluate the deterioration process accurately: the degraded zone, the strengthened zone, the invaded zone, and the intact zone.

Impact of Leaching and Chlorides on Sulfate Attack for Cement Paste

Pore Crystallization and Expansion of Cement Pastes in Sulfate Solutions with and Without Chlorides

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Effect of Layered Double Hydroxides on the Deterioration Process of Cement Paste under Sulfate Attack

A Model Investigation of the Mechanisms of External Sulfate Attack on Portland Cement Binders

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Experiments on Chloride Binding and Its Release by Sulfates in Cementitious Materials

The Stability of Bound Chlorides in Cement Paste with Sulfate Attack

Development of cementitious capillary crystalline waterproofing agents and durability study of concrete in the presence of chloride with sulfate in aqueous environment

Influence of internal sulfate attack on cement paste properties: contamination by pyrite

Microstructural evolution and degradation mechanisms of tricalcium silicate and tricalcium aluminate composite pastes under sulfate exposure

Sulfate Diffusivity Altered by Pore Crystallization Due to Chemical Sulfate Attack of Cement-Based Materials

Numerical simulation on the crystallization-induced mechanical response in hardened cement paste under external sulfate attack

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Research on Sulfate Attack Mechanism of Cement Concrete Based on Chemical Thermodynamics

Interaction between zeolite and sulfate, and its influences on cement hydration

Deterioration Process of Concrete Exposed to Internal Sulfate Attack

Microstructural origins of cement paste degradation by external sulfate attack