Abstract:Sulfate attack precipitates instability and degradation within calcium silicate (aluminate) hydrate (C-(A)-S-H) gel, the primary binding phase in cementitious materials. This degradation intricately correlates with the clinker phase composition, particularly the ratios of tricalcium silicate (C 3 S) and tricalcium aluminate (C 3 A). In this study, C 3 S and C 3 A were synthesized through solid-state sintering to create C 3 S-C 3 A pastes. The research aimed to examine the impact of varying C 3 A substitution levels and Na 2 SO 4 exposure durations on the microstructure and performance of these composite pastes. The findings reveal that C 3 A markedly accelerates both the early hydration kinetics and the overall hydration degree of C 3 S within the C 3 S-C 3 A system, with this effect becoming more pronounced with increasing C 3 A content. Furthermore, the inclusion of C 3 A elevates the Al[4]/Si ratio, mean chain length (MCL), and Ca/Si of the C-S-H gel. This leads to an increase in the overall porosity of the composite matrix while simultaneously diminishing its chloride-binding capacity. Exposure to Na 2 SO 4 disrupts the incorporation of Al 3+ , released during C 3 A hydration, into the bridging sites of the C-S-H structure, causing a decrease in the Al[4]/Si of the C-(A)-S-H gel. The leached aluminum subsequently reacts with SO 4 2- to form ettringite and other deleterious compounds. Additionally, Na 2 SO 4 exposure induces a significant reduction in the Ca/Si within the composite pastes, with the magnitude of decalcification inversely proportional to the initial Ca/Si—implying that higher C 3 A content exacerbates the decalcification process. During the process of sulfate attack, the formation of gypsum and AFt complicates the pore structure of the matrix, providing more adsorption sites for the binding of Cl - .

Pore Crystallization and Expansion of Cement Pastes in Sulfate Solutions with and Without Chlorides

A Multiscale Microstructure Model of Cement Paste Sulfate Attack by Crystallization Pressure

Impact of Leaching and Chlorides on Sulfate Attack for Cement Paste

A Model Investigation of the Mechanisms of External Sulfate Attack on Portland Cement Binders

Effect of Calcium Sulfate on the Formation of Ettringite in Calcium Aluminate and Sulfoaluminate Blended Systems

Sulfate Diffusivity Altered by Pore Crystallization Due to Chemical Sulfate Attack of Cement-Based Materials

Numerical Investigation on Gypsum and Ettringite Formation in Cement Pastes Subjected to Sulfate Attack

Examination of sulfate resistance of nano-alumina added ordinary Portland cement paste, focusing on the two different crystallinity of nano-aluminas

In Situ Observing the Erosion Process of Cement Pastes Exposed to Different Sulfate Solutions with X-ray Computed Tomography

Microstructural origins of cement paste degradation by external sulfate attack

Study on the Binding Behavior of Chloride Ion and Ettringite in Nano-Metakaolin Cement by Seawater Mixing and Curing Temperatures

Sulfate Crystallization Attack on Cement-Based Materials

Expansion Mechanism of C4A3$-CaSO4-CaO in Portland Cement Paste

Effect of Polycarboxylate Superplasticizers on the Growth of Ettringite in Deionized Water and Synthetic Cement Pore Solution

Impact of the Thaumasite Sulfate Attack on the Pore Structure and Gas Permeability of Cement Mortar

Microstructural evolution and degradation mechanisms of tricalcium silicate and tricalcium aluminate composite pastes under sulfate exposure

Numerical simulation on the crystallization-induced mechanical response in hardened cement paste under external sulfate attack

Deterioration Evolutive Process of Cement-Based Materials under Sulphate Physical Crystallization Attack

Changes of Pore Structure and Chloride Content in Cement Pastes after Pore Solution Expression

Mechanism of expansion of mortars immersed in sodium sulfate solutions

Effect of Pore Solution Expression on Solid Composition of Cement Paste