Abstract:Recycled aggregate concrete is a promising low carbon material, which need further analysis on the durability. To investigate the influence of sulfate erosion on recycled concrete made with high-belite sulfoaluminate cement (HBCSA), this study utilized compressive strength and microhardness test to evaluate the effect of sulfate on ITZ. Then by using backscattered electron imaging, scanning electron microscope and energy spectrometry, the mechanism for the microstructural changes that occurred before and after sulfate erosion is revealed. Results showed that after 60 days of sulfate erosion, both aggregate-new mortar and new–old mortar interfaces display reduced microhardness and widened transition zones. Specifically, in the C30 group post-erosion, the microhardness values for the aggregate-new mortar interface ranged from 50.3 to 66.9 MPa, while the new–old mortar interface exhibited a range of 47–77 MPa. Besides, the new–old mortar interface exhibit marginally superior sulfate resistance to the aggregate–new mortar interface at the same concrete strength grade. Moreover, sulfate resistance improvs across all interfaces with increasing strength class. For instance, in the aggregate-new mortar interface, the maximum microhardness post-erosion for C40 showed a 51.6 % increase compared to C30. Through microstructure analysis, it is found that after sulfate erosion, the aggregate–new mortar and new–old mortar interfaces of HBCSA recycled concrete are both enriched with abundant ettringite and gypsum, which causes considerable swelling erosive product formation and even cracking. The less formed cracks in new–old mortar interfaces results in the better sulfate resistance. The finding is helpful for the future research on the high sulfate resistant recycled aggregate concrete.

Internal sulfate attack in mortars containing contaminated fine recycled concrete aggregates

Damage mechanism of sulfate attack on recycled fine aggregate mortar

The Influence of External Sulfate Attack on the Durability of Reinforced Mortars in the Presence of Calcined River Sediments

Valorization of Fine Recycled Aggregates Contaminated with Gypsum Residues: Characterization and Evaluation of the Risk for Secondary Ettringite Formation

Influence of internal sulfate attack on cement paste properties: contamination by pyrite

Deterioration Process of Concrete Exposed to Internal Sulfate Attack

Effect of Exposure Conditions on Mortar Subjected to an External Sulfate Attack

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Mitigation potential of sulfate-resistant Portland cement for internal sulfate attack

Combined effect of alkali-aggregate reaction (AAR) and internal sulfate attack (ISA): Microstructural and porous structure modifications of portland cement mortars

Ultrasonic and impact spectroscopy monitoring on internal sulphate attack of cement-based materials

Durability of phosphogypsum-based supersulfated cement mortar against external attack by sodium and magnesium sulfate

Internal corrosion characteristics of endogenous sulfate introduced by recycled aggregates in recycled aggregates concrete: Insights into the macro-mechanical and meso-mechanical properties

Role of supplementary cementing materials on reducing damage due to internal sulphate attack in concrete

Iron sulfide-related internal sulfate attack: microstructure and mechanism

Research on the Sulfate-resistant Chemical Attack Mechanism of Concrete with Mineral Admixture

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Effect of sulfate attack on multiple interfacial transition zones of high-belite sulfoaluminate cement recycled concrete