Damage mechanism of sulfate attack on recycled fine aggregate mortar

Jian Geng

DOI: https://doi.org/10.13245/j.hust.140518

2014-01-01

Abstract:The influence of recycled fine aggregate (RFA ) content on the sulfate-resistance ability of mortar ,which immersed in sulfate sodium solution long time ,was researched by measured its com-pressive strength .The damage mechanism of RFA mortar was also studied by using IR (infrared) , XRD (X-ray powder diffraction) and SEM (scanning electron microscope) .The results indicate that the sulfate-resistance ability of mortar is weakened with the content of RFA increases ,especially for higher 40% river sand replacement ratio by RFA .The micro analysis shows that damage of RFA mor-tar immersed in sulfate sodium solution is induced by both ettringite and gypsum .But ,w hen the river sand replacement ratio is less than 20% ,ettringite is the dominant reason for the damage ,and then gypsum becomes the dominant factor with the ratio increases to 60% .In addition ,the amount of ettringite and gypsum also increase with the river sand replacement ratio improves .