Abstract:The incorporation of supplementary cementitious materials (SCMs) in concrete can improve the properties of concrete partially immersed in salt solution. However, the current partial immersion environment only considers the capillary action above the still water level, does not consider the capillary action above the fluctuating water level in dry-wet cycling environment. In this paper, a series of indoor exposure experiments were carried out to investigate the effects of incorporating polynary SCMs including fly ash (FA), ground granulated blast furnace slag (GGBFS) and silica fume (SF) on the sulfate resistance and chloride impermeability of concrete considering the capillary action above the fluctuating water level in dry-wet cycling environment. A total of 15 groups of concrete with different mix proportions (total 150 concrete specimens) were designed to study the effects of different replacement levels of polynary SCMs on concrete properties. The effects of incorporating polynary SCMs on the chloride impermeability of concrete above and in the fluctuating water level zone were investigated. The scanning electron microscope (SEM), x-ray diffraction (XRD) and mercury intrusion porosimetry (MIP) tests were used to analyze the microstructure of concrete. The results indicate that when concrete is incorporated with polynary SCMs and subjected to capillary action above the fluctuating water level, the compressive strength and chloride impermeability first increase and then decrease with the increase of FA content; the compressive strength and chloride impermeability decrease with the increase of GGBFS content; the compressive strength first increase and then decrease with the increase of SF content, and the chloride impermeability increase with that. The transport process of chloride in concrete above the fluctuating water level zone includes the longitudinal transport under capillary action and the transverse transport under concentration gradient action. The combined effects of both cause the higher chloride concentration in concrete above the fluctuating water level zone. Comprehensively considering the influence of different mix proportions on the sulfate resistance and chloride impermeability of concrete, it is determined that 20% FA + 5% SF is the optimal replacement level with the excellent performance considering the capillary action above the fluctuating water level in dry-wet cycling environment.

Roles of fly ash, granulated blast-furnace slag, and silica fume in long-term resistance to external sulfate attacks at atmospheric temperature

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Effect of steel slag powder, fly ash, and silica fume on the mechanical properties and durability of cement mortar

Evaluating Durability: A Comparative Study on the Influence of Fly Ash and Silica Fume in Potassium Magnesium Phosphate Cement Mortar

Effects of incorporating polynary SCMs on sulfate resistance and chloride impermeability of concrete considering capillary action in dry-wet cycling environment

Deterioration of Mortar Bars Using Binary and Ternary Mixtures Immersed in Sodium Sulfate Solutions

Long-term strength and durability performance of eco-friendly concrete with supplementary cementitious materials

Durability of blended cement against sodium sulphate attack and alkali-silica reaction

Influence of fly ash on mechanical properties and hydration of calcium sulfoaluminate-activated supersulfated cement

The long-term failure mechanisms of alkali-activated slag mortar exposed to wet-dry cycles of sodium sulphate

Effect of Nano-SiO2/PVA Fiber on Sulfate Resistance of Cement Mortar Containing High-Volume Fly Ash

Sulfate attack on concrete with mineral admixtures

Influence of Fly Ash Content on the Durability of Mortar Specimens under Dry/Wet Sulfate Attack

Durability of phosphogypsum-based supersulfated cement mortar against external attack by sodium and magnesium sulfate

Sulfate Resistance and Degradation Mechanism of Basalt Fiber Modified Graphite Tailings Cement-Based Materials

Resistance of blended alkali-activated fly ash-OPC mortar to mild-concentration sulfuric and acetic acid attack

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Effect of internal sulfate attack on the properties of sulfate-resisting cement and alkali-activated slag

Effect of Limestone Powder and Fly Ash on Magnesium Sulfate Resistance of Mortar