Abstract:This study assessed the impact of calcium silicate slag (CSS), an industrial by-product of aluminum extraction from fly ash, on the reaction kinetics, compressive strength, and efflorescence of one-part sodium carbonate-activated slag (SCS). Various proportions of CSS (0%, 10%, and 20%) were used to substitute for slag. The resulting performances were evaluated through chemical shrinkage, heat liberation, compressive strength, water absorption, phase composition (XRD and TG.), microstructures (BET and BSE-EDS), and simulated efflorescence test (partially and fully immersed in deionized water). The results indicate that the CSS possesses a porous structure. The addition of CSS impairs flowability but accelerates the development of chemical shrinkage and heat liberation. The incorporation of CSS promotes the transformation of gaylussite, leading to an increase in CASH and hydrotalcite formation. Consequently, a higher compressive strength and a lower water adsorption rate are achieved. 10% CSS addition improves the splitting tensile strength of SCS under conditions of partial immersion in the efflorescence test. However, a 20% CSS substitution exacerbates the formation of efflorescence products and reduces the splitting tensile strength. These observations are associated with residual alkalis in CSS, a lower Al/Si ratio of products, and an increase in capillary pores attributed to CSS particles. This paper demonstrates the feasibility of using alkaline solid waste for slag substitution and performance regulation in SCS and reveals the underlying mechanism. The prepared CSS-SCS binder exhibits much lower energy consumption and CO2 emission than traditional cement-based material, as determined by life cycle assessment.

Effect of internal sulfate attack on the properties of sulfate-resisting cement and alkali-activated slag

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Evaluation of Sulfate Resistance of Calcined Dolomite Activated Ground Granulated Blast Furnace Slag

Reaction mechanism of sulfate attack on alkali-activated slag/fly ash cements

Hydration and Properties of Slag Cement Activated by Alkali and Sulfate

Effect of Slaked Lime on the Properties of Sodium Sulfate-Activated Alkali-Activated Slag Cement

Investigation of effects of reactive MgO on autogenous and drying shrinkage of near-neutral salt activated slag cement

Effect of Mineral Admixtures on Sulfate Attack Resistance of Cement-Based Materials

Sulfate Resistance of Carbonated Basic Oxygen Furnace Slag-Metakaolin-portland Cement Blends

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Strength and Drying Shrinkage of Reactive MgO Modified Alkali-Activated Slag Paste

The long-term failure mechanisms of alkali-activated slag mortar exposed to wet-dry cycles of sodium sulphate

Effect of Alkali Sulfates in Clinker on Hydration and Hardening Properties of Cement Incorporating SCMs

Mechanisms and Differences Between Sodium and Magnesium Sulfate Attacks on Alkali-Activated Phosphorus Slag

Degradation Mechanism of Slag Blended Mortars Immersed in Sodium Sulfate Solution

Mechanical Performance and Durability of Mortar Based on Slag Cement and NaOH-Activated Slag

Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars

Upcycling sulphidic copper tailings into alkali-activated slag materials: effect of the sulfur content

Effect of blended inorganic salts containing negative hydration ions on hydration and properties of alkali-activated slag cement

The role of CaO and MgO incorporation in chloride resistance of sodium carbonate-activated slag