Properties of Alkali-Activated Slag Cement Activated by Weakly Alkaline Activator

Juan He,Shuya Yu,Guochen Sang,Junhong He,Jie Wang,Zheng Chen
DOI: https://doi.org/10.3390/ma16103871
IF: 3.4
2023-05-22
Materials
Abstract:Sodium sulfate (Na2SO4) and sodium carbonate (Na2CO3) are weakly alkaline activators. Alkali-activated slag (AAS) cement prepared with them shows the special advantages of long setting time and low shrinkage, but it shows slow development of mechanical properties. In the paper, Na2SO4 and Na2CO3 were used as activators and compounded with reactive magnesium oxide (MgO) and calcium hydroxide (Ca(OH)2) to optimize the setting time and mechanical properties. The hydration products and microscopic morphology were also studied using XRD, SEM, and EDS. Furthermore, the production cost and environmental benefits were compared and analyzed. The results show that Ca(OH)2 is the main influencing factor for setting time. It reacts preferentially with Na2CO3 to form CaCO3, which makes AAS paste lose plasticity rapidly and shortens the setting time, and then produces strength. Na2SO4 and Na2CO3 are the main influencing factors for flexural and compressive strength, respectively. Suitably high content is beneficial to promote the development of mechanical strength. The interaction of Na2CO3 and Ca(OH)2 shows a great effect on the initial setting time. High content of reactive MgO can shorten the setting time and increase the mechanical strength at 28 days. There are more crystal phases in hydration products. Considering the setting time and mechanical properties, the composition of activators are: 7% Na2SO4, 4% Na2CO3, 3–5% Ca(OH)2, and 2–4% reactive MgO. Compared with ordinary Portland cement (OPC) and AAS cement activated by sodium hydroxide (NaOH, NH) and water glass (WG) with the same alkali equivalent, the production cost and energy consumption are greatly reduced. Compared with P·O 42.5 of OPC, CO2 emission is reduced by 78.1%. AAS cement activated by weakly alkaline activators shows excellent environmental and economic benefits and good mechanical properties.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on how to optimize the setting time and mechanical properties of alkali - activated slag cement (AAS cement) by using weakly alkaline activators (such as sodium sulfate \( \text{Na}_2\text{SO}_4 \) and sodium carbonate \( \text{Na}_2\text{CO}_3 \)). Specifically: 1. **Optimization of setting time**: - In the study, sodium sulfate (\( \text{Na}_2\text{SO}_4 \)), sodium carbonate (\( \text{Na}_2\text{CO}_3 \)), reactive magnesia (MgO) and calcium hydroxide (Ca(OH)_2) were used as composite activators to optimize the setting time of AAS cement. - Calcium hydroxide (Ca(OH)_2) is the main factor affecting the initial setting time. It preferentially reacts with sodium carbonate to produce calcium carbonate (CaCO_3), causing the AAS paste to rapidly lose plasticity, shorten the setting time, and subsequently develop strength. - Sodium sulfate (\( \text{Na}_2\text{SO}_4 \)) and sodium carbonate (\( \text{Na}_2\text{CO}_3 \)) are the main factors affecting the flexural strength and compressive strength respectively. An appropriately high content of these activators is beneficial to promoting the development of mechanical properties. - A high content of reactive magnesia (MgO) can shorten the 28 - day setting time and increase the mechanical strength. 2. **Improvement of mechanical properties**: - The study analyzed the influence of each activator on the setting time and mechanical properties through orthogonal experimental design, and obtained the optimal activator combination: 7% \( \text{Na}_2\text{SO}_4 \), 4% \( \text{Na}_2\text{CO}_3 \), 3 - 5% Ca(OH)_2, 2 - 4% reactive MgO. - This optimized activator combination not only shortens the setting time, but also significantly improves the 28 - day flexural and compressive strengths. 3. **Environmental and economic benefits**: - Compared with ordinary Portland cement (OPC) and AAS cement activated with sodium hydroxide (NaOH) or water glass (sodium silicate), AAS cement using weakly alkaline activators has significant advantages in production cost, energy consumption and carbon dioxide emissions. - Specifically, compared with P·O 42.5 OPC, AAS cement using weakly alkaline activators can reduce carbon dioxide emissions by 78.1%. In conclusion, this paper aims to improve the setting time and mechanical properties of AAS cement by optimizing the types and proportions of activators, while reducing production costs and environmental impacts, thereby promoting its wide use in engineering applications.