Abstract:Composites that use fly ash and slag as alkali-activated materials instead of cement can overcome the defects and negative effects of alkali-activated cementitious materials prepared with the use of an alkali-activated material. In this study, fly ash and slag were used as raw materials to prepare alkali-activated composite cementitious materials. Experimental studies were carried out on the effects of the slag content, activator concentration and curing age on the compressive strength of the composite cementitious materials. The microstructure was characterized using hydration heat, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), and its intrinsic influence mechanism was revealed. The results show that increasing the curing age improves the degree of polymerization reaction and the composite reaches 77~86% of its 7-day compressive strength after 3 days. Except for the composites with 10% and 30% slag content, which reach 33% and 64%, respectively, of their 28-day compressive strength at 7 days, the remaining composites reach more than 95%. This result indicates that the alkali-activated fly ash–slag composite cementitious material has a rapid hydration reaction in the early stage and a slow hydration reaction in the later stage. The amount of slag is the main influencing factor of the compressive strength of alkali-activated cementitious materials. The compressive strength shows a trend of continuous increase when increasing slag content from 10% to 90%, and the maximum compressive strength reaches 80.26 MPa. The increase in the slag content introduces more Ca2+ into the system, which increases the hydration reaction rate, promotes the formation of more hydration products, refines the pore size distribution of the structure, reduces the porosity, and forms a denser microstructure. Therefore, it improves the mechanical properties of the cementitious material. The compressive strength shows a trend of first increasing and then decreasing when the activator concentration increases from 0.20 to 0.40, and the maximum compressive strength is 61.68 MPa (obtained at 0.30). The increase in the activator concentration improves the alkaline environment of the solution, optimizes the level of the hydration reaction, promotes the formation of more hydration products, and makes the microstructure denser. However, an activator concentration that is too large or too small hinders the hydration reaction and affects the strength development of the cementitious material.

The Effect of Alkaline Activator on Workability and Compressive Strength of Alkali-Activated Slag Concrete

Preparation of Coal Gasification Coarse Slag-Based Alkaline Activator and Its Activation Mechanism in Alkali-Activated Slag

Effect of binder and activator composition on the characteristics of alkali-activated slag-based concrete

Effect of activator concentration on setting time, workability and compressive strength of sustainable concrete with alkali-activated slag binder

Properties of Alkali-Activated Slag Cement Activated by Weakly Alkaline Activator

Study of the Mechanical Properties and Microstructure of Alkali-Activated Fly Ash–Slag Composite Cementitious Materials

The Effect of Blast Furnace Slag/Fly Ash Ratio on Setting, Strength, and Shrinkage of Alkali-Activated Pastes and Concretes

Strength Analysis and Optimization of Alkali Activated Slag Backfills Through Response Surface Methodology

Using calcium carbide residue to prepare ecological alkali activated slag composites: Effect of anion type

Effect of Alkaline-Earth Metal Oxide on Compressive Strength and Flexural Strength of Alkali-Activated Slag Cement Mortar

Influence of alkali content and silica modulus on the carbonation kinetics of alkali-activated slag concrete

Alkali-activated slag (AAS) paste: Correlation between durability and microstructural characteristics

RSM-based Optimized Mix Design of Alkali-activated Slag Pastes Based on the Fresh and Hardened Properties and Unit Cost

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Effect of activator on rheological properties of alkali-activated slag-fly ash pastes

Approach to design sustainable alkali-activated slag recycled aggregate concrete: Mechanical and microstructural characterization

Early mechanical properties and strength calculation method of slag-based alkali activated concrete

Effect of Slaked Lime on the Properties of Sodium Sulfate-Activated Alkali-Activated Slag Cement

Effect of internal sulfate attack on the properties of sulfate-resisting cement and alkali-activated slag

A novel admixture to improve durability of alkali-activated slag by reducing water sorptivity and optimising the process of activation

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents