Abstract:Sodium sulfate (Na2SO4) and sodium carbonate (Na2CO3) are weakly alkaline activators. Alkali-activated slag (AAS) cement prepared with them shows the special advantages of long setting time and low shrinkage, but it shows slow development of mechanical properties. In the paper, Na2SO4 and Na2CO3 were used as activators and compounded with reactive magnesium oxide (MgO) and calcium hydroxide (Ca(OH)2) to optimize the setting time and mechanical properties. The hydration products and microscopic morphology were also studied using XRD, SEM, and EDS. Furthermore, the production cost and environmental benefits were compared and analyzed. The results show that Ca(OH)2 is the main influencing factor for setting time. It reacts preferentially with Na2CO3 to form CaCO3, which makes AAS paste lose plasticity rapidly and shortens the setting time, and then produces strength. Na2SO4 and Na2CO3 are the main influencing factors for flexural and compressive strength, respectively. Suitably high content is beneficial to promote the development of mechanical strength. The interaction of Na2CO3 and Ca(OH)2 shows a great effect on the initial setting time. High content of reactive MgO can shorten the setting time and increase the mechanical strength at 28 days. There are more crystal phases in hydration products. Considering the setting time and mechanical properties, the composition of activators are: 7% Na2SO4, 4% Na2CO3, 3–5% Ca(OH)2, and 2–4% reactive MgO. Compared with ordinary Portland cement (OPC) and AAS cement activated by sodium hydroxide (NaOH, NH) and water glass (WG) with the same alkali equivalent, the production cost and energy consumption are greatly reduced. Compared with P·O 42.5 of OPC, CO2 emission is reduced by 78.1%. AAS cement activated by weakly alkaline activators shows excellent environmental and economic benefits and good mechanical properties.

Preparation of Coal Gasification Coarse Slag-Based Alkaline Activator and Its Activation Mechanism in Alkali-Activated Slag

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Comparison of Mechanical Properties and Microstructure of GGBS-based Cementitious Materials Activated by Different Combined Alkaline Wastes

Effect of Alkali and Sulfate on the Hydration Characteristic of Cement-Based Materials Containing Coal Gasification Slag

The Influence of Alkaline Activation on Coal Gasification Slag–mswi FA Based Binder and Its Associated Hydration Mechanism

Preparation and characterization of cementitious materials based on sulfuric-acid-activated coal gasification coarse slag

Preparation and Reaction Mechanism Characterization of Alkali-activated Coal Gangue–Slag Materials

Physical-chemical Performance of Coal Gasification Slag with Calcination Activation Utilized As Supplementary Cementitious Material

A novel admixture to improve durability of alkali-activated slag by reducing water sorptivity and optimising the process of activation

Properties of Alkali-Activated Slag Cement Activated by Weakly Alkaline Activator

Study on the excitation effect and mechanism of coal gasification slag based on solid waste

Using calcium carbide residue to prepare ecological alkali activated slag composites: Effect of anion type

Effects of Mechanical Activation on Physical and Chemical Characteristics of Coal-Gasification Slag

Rheology, Mechanical Properties, and Hydration of Synergistically Activated Coal Gasification Slag with Three Typical Solid Wastes

Study on Activity Characteristics of Modified Coal Gasification Coarse Slag and Its Hydration Hardening Properties of Blended Cement Paste

Enhancement of Setting Times and Hardening of Alkali-Activated Slag Binder Using CO2-modified Slag

Ground Granulated Blast-Furnace Slag/fly Ash Blends Activated by Sodium Carbonate at Ambient Temperature

Steel Slag for Carbon Fixation and Synthesis of Alkali-Activated Material

Microstructure and Mechanical Properties of Activated High-Alumina Ferronickel Slag with Carbide Slag and Alkaline Salts

Alkali-activated slag supplemented with waste glass powder: Laboratory characterization, thermodynamic modelling and sustainability analysis

Mechanical Properties and Durability of Alkali-Activated Steel Slag–blastfurnace Slag Cement