Abstract:Using granulated blast furnace slag (GGBS) as the volcanic ash material and fly ash (FA) as the supplementary material, the study was conducted to investigate the mix proportions of an alkali-activated solid waste cementitious material under the stimulating effect of alkali activator carbide slag (CS). This type of cementitious material could serve as a substitute for a portion of cement usage, contributing to resource conservation and mitigating environmental pollution caused by solid waste. This facilitates green and sustainable development. Firstly, an analysis of three raw materials was conducted, and the mix proportions were designed with reference to the CaO-Al 2 O 3 -SiO 2 system of Portland cement. Then 28 groups of specimens were prepared based on the designed mix proportions. The flowability and setting time of each group of specimens were tested. It was observed that an increase in the amount of CS and a decrease in the amount of GGBS resulted in decreased flowability and earlier setting times of the specimens. Additionally, FA exhibited a retarding effect on setting time. Compressive strength tests were conducted on these specimens, revealing that the optimal CS content ranged between 20 % and 40 %. Overall, FA had minimal impact on compressive strength, but it contributed to increased compressive strength in the specimens at later ages. Subsequently, microscopic characterization of the hydration products was performed using X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR), Differential Thermal Analysis (DTA), Scanning Electron Microscope (SEM), and Energy Dispersive Spectrometer (EDS). The hydration products were identified as predominantly composed of calcium silicate hydrate. The quality and defects in the microstructure of gel products from various specimen formulations were compared to elucidate differences in macroscopic performance. Finally, the hydration process mechanism diagram of alkali-activated materials was presented to illustrate the stimulation and formation of gel products, primarily composed of C-S-H. This diagram revealed the principles behind the action of alkali-activated cementitious materials. The proposed design and testing methodology for the GGBS-FA-CS system in this study had certain reference significance for research in the direction of alkali-activated solid waste cementitious materials.

Sodium carbonate-enhanced calcium carbide slag activation of sewage sludge for the preparation of green cementitious materials

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Preparation of Coal Gasification Coarse Slag-Based Alkaline Activator and Its Activation Mechanism in Alkali-Activated Slag

Carbide slag and sodium metasilicate synergistic activation of sludge ash-based alkali-activated materials: Towards a cleaner activation approach

Optimization of Calcium Carbide Residue Utilization for Producing High‐quality Calcium Carbonate

Using calcium carbide residue to prepare ecological alkali activated slag composites: Effect of anion type

Accelerating the Reaction Kinetics of Na2CO3-Activated Slag Mortars by Calcined Recycled Concrete Fines

Study on the Properties and Hydration Mechanism of Calcium Carbide Residue-Based Low-Carbon Cementitious Materials

Compressive Strength and Gel Structure Improvement in the High-Volume Calcium Carbide Residue Activated-Blast Furnace Slag System Combined with Sodium Carbonate and Silica Fume

Effect of Calcium Carbide Residue on Strength Development along with Mechanisms of Cement-Stabilized Dredged Sludge

Synergistic Activation Mechanism and Long-Term Properties of a Solid Waste Cementitious Materials Based on Red Mud and Calcium Carbide Slag

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Utilization of Sintered Sludge Ash with Different Mechanical–Thermal Activation Parameters as a Supplementary Cementitious Material: Mechanical Properties and Life Cycle Assessment of Cement-Based Paste

Comparison of Mechanical Properties and Microstructure of GGBS-based Cementitious Materials Activated by Different Combined Alkaline Wastes

Effect of Alkali and Sulfate on the Hydration Characteristic of Cement-Based Materials Containing Coal Gasification Slag

Study on the Alkali–Sulfur Co-Activation and Mechanical Properties of Low-Carbon Cementitious Composite Materials Based on Electrolytic Manganese Residue, Carbide Slag, and Granulated Blast-Furnace Slag

Effect of carbide slag and steel slag as alkali activators on the key properties of carbide slag-steel slag-slag-phosphogypsum composite cementitious materials

Microstructure of Portland Cement Blended with High Dosage of Sewage Sludge Ash Activated by Na2SO4

Optimization of eco-friendly materials by alkali activation of the sewage sludge ash (SSA) to reduce carbon footprint

Study on the preparation, performance, and mechanism for solid waste cementitious materials

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents