Abstract:Using granulated blast furnace slag (GGBS) as the volcanic ash material and fly ash (FA) as the supplementary material, the study was conducted to investigate the mix proportions of an alkali-activated solid waste cementitious material under the stimulating effect of alkali activator carbide slag (CS). This type of cementitious material could serve as a substitute for a portion of cement usage, contributing to resource conservation and mitigating environmental pollution caused by solid waste. This facilitates green and sustainable development. Firstly, an analysis of three raw materials was conducted, and the mix proportions were designed with reference to the CaO-Al 2 O 3 -SiO 2 system of Portland cement. Then 28 groups of specimens were prepared based on the designed mix proportions. The flowability and setting time of each group of specimens were tested. It was observed that an increase in the amount of CS and a decrease in the amount of GGBS resulted in decreased flowability and earlier setting times of the specimens. Additionally, FA exhibited a retarding effect on setting time. Compressive strength tests were conducted on these specimens, revealing that the optimal CS content ranged between 20 % and 40 %. Overall, FA had minimal impact on compressive strength, but it contributed to increased compressive strength in the specimens at later ages. Subsequently, microscopic characterization of the hydration products was performed using X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR), Differential Thermal Analysis (DTA), Scanning Electron Microscope (SEM), and Energy Dispersive Spectrometer (EDS). The hydration products were identified as predominantly composed of calcium silicate hydrate. The quality and defects in the microstructure of gel products from various specimen formulations were compared to elucidate differences in macroscopic performance. Finally, the hydration process mechanism diagram of alkali-activated materials was presented to illustrate the stimulation and formation of gel products, primarily composed of C-S-H. This diagram revealed the principles behind the action of alkali-activated cementitious materials. The proposed design and testing methodology for the GGBS-FA-CS system in this study had certain reference significance for research in the direction of alkali-activated solid waste cementitious materials.

Synergistic Activation Mechanism and Long-Term Properties of a Solid Waste Cementitious Materials Based on Red Mud and Calcium Carbide Slag

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Study on the Alkali–Sulfur Co-Activation and Mechanical Properties of Low-Carbon Cementitious Composite Materials Based on Electrolytic Manganese Residue, Carbide Slag, and Granulated Blast-Furnace Slag

Optimization of Proportions and Solidification Mechanism of All-Solid Waste Cementitious Materials Based on Circulating Fluidized Bed Fly Ash, Calcium Carbide Slag, and Red Mud

The synergistic hydration mechanism and environmental safety of multiple solid wastes in red mud-based cementitious materials

Study on the preparation, performance, and mechanism for solid waste cementitious materials

Strength formation mechanism and curing system optimization of low-carbon cementitious materials prepared by synergistic activation of multiple alkaline solid wastes

Utilization of municipal solid waste incineration fly ash with red mud-carbide slag for eco-friendly geopolymer preparation

Mechanical Properties and Mechanism of Geopolymer Cementitious Materials Synergistically Prepared Using Red Mud and Yellow River Sand

Study on the Properties and Hydration Mechanism of Calcium Carbide Residue-Based Low-Carbon Cementitious Materials

Upcycling use of red mud-based solid waste in engineered cementitious composites: Properties, activation mechanism, and life-cycle assessment

Mechanical properties and chemical microscopic characteristics of all-solid-waste composite cementitious materials prepared from phosphogypsum and granulated blast furnace slag

The Use of Slag and Red Mud for the Synthesis of a Slag-Based Cementitious Material

Hydration Mechanisms of Alkali-Activated Cementitious Materials with Ternary Solid Waste Composition

Preparation and curing method of red mud-calcium carbide slag synergistically activated fly ash-ground granulated blast furnace slag based eco-friendly geopolymer

Production of a new type of cemented paste backfill with solid waste from carbide slag, soda residue, and red mud: mechanism, optimization, and its environmental effects

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Utilization of Copper–Molybdenum Tailings to Enhance the Compressive Strength of Alkali-Activated Slag-Fly Ash System

Sodium carbonate-enhanced calcium carbide slag activation of sewage sludge for the preparation of green cementitious materials

Mechanical properties and environmental characteristics of the synergistic preparation of cementitious materials using electrolytic manganese residue, steel slag, and blast furnace slag

Designing low-carbon fly ash based geopolymer with red mud and blast furnace slag wastes: Performance, microstructure and mechanism