Abstract:Alkali-activated cementitious materials, as an environmentally friendly cementitious material, can effectively reduce carbon emissions and improve the utilisation of solid wastes. However, traditional strong alkali activators have limitations such as high carbon emissions and poor safety. In order to overcome the defects of traditional strong alkaline activators and realise the high value-added use of calcium carbide residue (CCR), this paper adopts CCR as an alkaline activator to activate granulated blast furnace slag (GBFS)-steel slag (SS) cementitious systems for the preparation of alkaline-activated cementitious materials. The effects of CCR content and SS content on the compressive strength and working performance of CCR-GBFS-SS cementitious systems are analysed, along with the hydration process of CCR-GBFS-SS cementitious systems and the mechanism of action through the hydration products, their chemical structure and their microscopic morphology. The research results show that CCR-GBFS-SS cementitious systems have a 28-day compressive strength of 41.5 MPa and they can be controlled by the setting time; however, the flow performance is poor. The SS content can be increased to improve the flow performance; however, this will reduce the compressive strength. In CCR-GBFS-SS cementitious systems, CCR is the main driving force of hydration reactions, GBFS mainly provides active silica and aluminium and the amorphous C-(A)-S-H gel and ettringite formed by the synergistic action of multiple solid wastes are the main sources of compressive strength. With the extension of the curing time, the amount of hydration products in the cementitious systems gradually increases and the matrix of the cementitious systems gradually becomes denser. This study will provide a reference for the consumption of low-value solid waste such as CCR and the preparation of low-carbon cementitious materials from multi-component solid wastes.

Mechanism of Na2CO3 on Early Properties of Red Mud-Based Alkali-Activated Cementitious Materials

Effects of Red Mud on Workability and Mechanical Properties of Autoclaved Aerated Concrete (AAC)

Preparation and performance of AACM with red mud and GGBFS: effectiveness of alkali activator

C-A-S-H Gel and Pore Structure Characteristics of Alkali-Activated Red Mud–Iron Tailings Cementitious Mortar

Early Age Properties of Alkali-Activated Cement and Class G Cement under Different Saturation Conditions in Oil Well Applications

Accelerating the Reaction Kinetics of Na2CO3-Activated Slag Mortars by Calcined Recycled Concrete Fines

Utilization of Red Mud with High Radiation for Preparation of Autoclaved Aerated Concrete (AAC): Performances and Microstructural Analysis

Effect of pore structure characteristics on the properties of red mud-based alkali-activated cementitious materials

Sodium carbonate-enhanced calcium carbide slag activation of sewage sludge for the preparation of green cementitious materials

Long-term performance of novel high-calcium one-part alkali-activated cement developed from thermally activated lime kiln dust

Alkali-activated red mud in stabilizing marine dredged clay with low amount of cement

Synergistic Activation Mechanism and Long-Term Properties of a Solid Waste Cementitious Materials Based on Red Mud and Calcium Carbide Slag

Strengthening Mechanism of Red Mud with Calcium Oxide

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Physical and Chemical Relationships in Accelerated Carbonation Conditions of Alkali-Activated Cement Based on Type of Binder and Alkali Activator

Properties of Alkali-Activated Slag Cement Activated by Weakly Alkaline Activator

Alkali activated cement mixture at ambient curing: Strength, workability, and setting time

Effect of borax-modified activator on mechanical properties and drying shrinkage of alkali-activated slag/metakaolin mortar

Study on the Properties and Hydration Mechanism of Calcium Carbide Residue-Based Low-Carbon Cementitious Materials

Early mechanical properties and strength calculation method of slag-based alkali activated concrete

Properties of Alkali-Activated Concrete Made Using the Optimum Combinations of Precursor Materials and Activation Parameters