Abstract:Red mud (RM) is an industrial waste generated in the process of aluminum refinement. The recycling and reusing of RM have become urgent problems to be solved. To explore the feasibility of using RM in geotechnical engineering, this study combined magnesium oxide (MgO) (or calcium oxide (CaO)) with RM as an RM-based binder, which was then used to stabilize the soil. The physical, mechanical, and micro-structural properties of the stabilized soil were investigated. As the content of MgO or CaO in the mixture increased, the unconfined compressive strength (UCS) of the RM-based cementitious materials first increased and then decreased. For the soils stabilized with RM–MgO or RM–CaO, the UCS increased and then decreased, reaching a maximum at RM:MgO = 5:5 or RM:CaO = 8:2. The addition of sodium hydroxide (NaOH) promoted the hydration reaction. The UCS enhancement ranged from 8.09% to 66.67% for the RM–MgO stabilized soils and 204.6% to 346.6% for the RM–CaO stabilized soils. The optimum ratio of the RM–MgO stabilized soil (with NaOH) was 2:8, while that of the RM–CaO stabilized soil (with NaOH) was 4:6. Freeze–thaw cycles reduced the UCS of the stabilized soil, but the resistance of the stabilized soil to freeze–thaw erosion was significantly improved by the addition of RM–MgO or RM–CaO, and the soil stabilized with RM–MgO had better freeze–thaw resistance than that with RM–CaO. The hydrated magnesium silicate generated by the RM–MgO stabilized soil and the hydrated calcium silicate generated by the RM–CaO stabilized soil helped to improve the UCS of the stabilized soil. The freeze–thaw cycles did not weaken the formation of hydration products in the stabilized soil but could result in physical damage to the stabilized soils. The decrease in the UCS of the stabilized soil was mainly due to physical damage.

Strengthening Mechanism of Red Mud with Calcium Oxide

Effects of Red Mud on Workability and Mechanical Properties of Autoclaved Aerated Concrete (AAC)

Study on Mechanism of Muddy Soil Stabilization

Engineering Properties and Microstructure of Soils Stabilized by Red-Mud-Based Cementitious Material

Alkali-activated red mud in stabilizing marine dredged clay with low amount of cement

Utilization of Red Mud with High Radiation for Preparation of Autoclaved Aerated Concrete (AAC): Performances and Microstructural Analysis

Binary reaction behaviors of red mud based cementitious material:Hydration characteristics and Na+ utilization

Solidification Mechanism of Bayer Red Mud under the Action of Calcium Hydroxide

Experimental Study on the Curing Mechanism of Red Mud-Based Stabilized Soil Co-Modified by Nano-SiO2 and Gypsum

Properties of Red-Mud-Modified Basic Magnesium Sulfate Cement

Effect of Red Mud on Mechanical Properties of Loess–Containing Aluminosilicate Based Cementitious Materials

Evaluation of blends bauxite-calcination-method red mud with other industrial wastes as a cementitious material: properties and hydration characteristics.

Preparation of building materials from Bayer red mud with magnesium cement

Unlocking the Role of Recycled Aggregates in the Performance Enhancement and CO2 Capture of Reactive Magnesia Cement Formulations

Effect of red mud and phosphate on water resistance and hydration mechanism of magnesium oxychloride cement

Preparation sequences and pretreatment optimization of alkali-activated red mud and blast furnace slag-based materials

Preparation mechanism and properties of thermal activated red mud and its geopolymer repair mortar

Synergistic Activation Mechanism and Long-Term Properties of a Solid Waste Cementitious Materials Based on Red Mud and Calcium Carbide Slag

Utilization of red mud for producing a high strength binder by composition optimization and nano strengthening

Mechanism of Na2CO3 on Early Properties of Red Mud-Based Alkali-Activated Cementitious Materials

The synergistic hydration mechanism and environmental safety of multiple solid wastes in red mud-based cementitious materials