Abstract:Red mud is a solid waste residue from the caustic soda leaching of bauxite ores to produce alumina by the Bayer process. Red mud contains large quantity of alkali and aluminosilicate, so it is potentially available to prepare inorganic polymeric materials by geopolymerisation process. However, the activity or dissolubility of the aluminosilicate phases in red mud is significantly poor, which constraints the geopolymerisation process. Therefore, some pretreatment process for red mud is necessary to improve the adhesive property and dissolubility of Bayer red mud. In this study, mineral phase transformation and dissolubility of a typical red mud sample were studied under different thermal treatment processes. The thermal behavior of the red mud was studied by TG-DTA. The crystalline phases of the samples calcined at 200–1000 °C for different hours were determined by XRD, and the dissolubility was determined by alkaline leaching test. The TG-DTA pattern shows no obvious endothermic or exothermic peaks, and the weight loss increases continuously as the temperature rises, which indicates that the crystalline phases transform continuously as the temperature rises, consistent with the XRD results. As the calcination temperature rises from 200 to 800 °C, several kinds of crystalline phase in original red mud, including gibbsite, katoite, muscovite, natrodavyne disappeared in succession, accompanied with the formation of nepheline, gehlenite, sodium aluminum silicate, and some amorphous aluminosilicate. The calcined products are more likely to dissolve. But when it rises over than 800 °C, the content of gehlenite increases, and the phase of which is stable. As the calcination temperature rises from 200 to 1000 °C, the dissolubility of aluminosilicate in the red mud under high alkaline conditions increases firstly and then decreases after over 800 °C. Therefore, the optimum temperature of thermal treatment for red mud is about 800 °C. This study could contribute to the following preparation of geopolymeric material made from red mud, especially the pretreatment process of red mud.

Solidification Mechanism of Bayer Red Mud under the Action of Calcium Hydroxide

Experimental Investigation on Red Mud from the Bayer Process for Cemented Paste Backfill

Utilization of Bayer red mud by a calcification–carbonation method using calcium aluminate hydrate as a calcium source

Strengthening Mechanism of Red Mud with Calcium Oxide

Direct Calcification–Carbonation Method for Processing of Bayer Process Red Mud

Engineering Properties and Microstructure of Soils Stabilized by Red-Mud-Based Cementitious Material

The synergistic hydration mechanism and environmental safety of multiple solid wastes in red mud-based cementitious materials

Recovery of Alkali and Alumina from Bayer Red Mud by the Calcification–carbonation Method

Preparation of geopolymer concrete with Bayer red mud and its reaction mechanism

Treatment of Bayer-Process Red Mud through Microbially Induced Carbonate Precipitation

Transformation and Characterization of Cement Clinker Prepared from New Structured Red Mud by Sintering

Alkali-activated red mud in stabilizing marine dredged clay with low amount of cement

Effects of Calcination on the Cementitious Activity and Pozzolanic Reactivity of Bayer Red Mud from Different Sources

Material properties and environmental implications of red mud solidified with blast-furnace slag, silica fume, and sodium hydroxide

Binary reaction behaviors of red mud based cementitious material:Hydration characteristics and Na+ utilization

Utilization of Red Mud and Pb/Zn Smelter Waste for the Synthesis of a Red Mud-Based Cementitious Material

Preparation and Properties of Alkali-Activated Red Mud-Based Artificial Lightweight Aggregates

The Effect of Incorporation of Red Mud on the Properties of Clay Ceramic Bodies

Synthesis and characterization of new acid-activated red mud-metakaolin geopolymers and comparison with their alkaline counterparts

Analysis of Alkali in Bayer Red Mud: Content and Occurrence State in Different Structures

Influence of Thermal Treatment on Phase Transformation and Dissolubility of Aluminosilicate Phase in Red Mud