Physical and Chemical Relationships in Accelerated Carbonation Conditions of Alkali-Activated Cement Based on Type of Binder and Alkali Activator

Yuto Yamazaki,Jihoon Kim,Keisuke Kadoya,Yukio Hama
DOI: https://doi.org/10.3390/polym13040671
IF: 5
2021-02-23
Polymers
Abstract:Alkali-activated cements prepared from aluminosilicate powders, such as blast furnace slag and fly ash, are rapidly attracting attention as alternatives to cement because they can significantly reduce CO2 emissions compared to conventional cement concrete. In this study, we investigated the relationship between the physical and chemical changes by accelerated carbonation conditions of alkali-activated cements. Alkali-activated cements were prepared from binders composed of blast furnace slag and fly ash as well as alkali activators sodium silicate and sodium hydroxide. Physical changes were analyzed from compressive strength, pH, and neutralization depth, and chemical changes were analyzed from XRD, TG-DTG, and 29Si MAS NMR. The C–(N)–A–S–H structure is noted to change via carbonation, and the compressive strength is observed to decrease. However, in the case of Na-rich specimens, the compressive strength does not decrease by accelerated carbonation. This work is expected to contribute to the field of alkali-activated cements in the future.
polymer science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the relationship between the physical and chemical changes of alkali - activated cements based on different binders and alkaline activators under accelerated carbonation conditions. Specifically, the author experimentally explored the effects of different types of binders (such as blast furnace slag and fly ash) and alkaline activators (such as sodium silicate and sodium hydroxide) on the physical properties (such as compressive strength, pH value, and neutralization depth) and chemical properties (such as X - ray diffraction XRD, thermogravimetric/differential scanning calorimetry TG - DTG, 29Si magic - angle - spinning nuclear magnetic resonance 29Si MAS NMR) of alkali - activated cements under accelerated carbonation conditions. The main purpose of the study is to evaluate the physical and chemical changes of different binders and alkaline activators in an accelerated carbonation environment and to understand the relationship between these changes and the carbonation mechanism. ### Research Background Ordinary Portland cement (OPC) is the main material for traditional concrete structures. A large amount of carbon dioxide (CO2) is released during its production process, which mainly comes from the process of carbonate (mainly CaCO3 in limestone) decomposing into oxides (mainly lime CaO) and CO2 (\[ \text{CaCO}_3 \rightarrow \text{CaO} + \text{CO}_2\uparrow \]). In addition, a large amount of fossil fuels need to be burned during the production process at a temperature of about 1400°C. Therefore, the production of 1 ton of Portland cement usually emits about 0.75 to 0.85 tons of CO2. The total CO2 emissions in the cement industry have increased rapidly in recent years, accounting for about 4% of Japan's total CO2 emissions and about 8% of the global total emissions, becoming the third - largest source of anthropogenic CO2 emissions. In order to reduce CO2 emissions, researchers have begun to focus on alkali - activated cements (AACs). Alkali - activated cements are composed of aluminosilicate powders (such as blast furnace slag, fly ash, and metakaolin) and alkaline activators (such as sodium silicate and sodium hydroxide). Compared with OPC, alkali - activated cements do not involve a hydration reaction during the hardening process. Instead, silicate ions (Si4+), aluminum ions (Al3+), and calcium ions (Ca2+) are dissolved from the binder and react with the alkaline activator to form hydration products. Studies have shown that alkali - activated cements can reduce CO2 emissions by about 80% and have excellent strength development, better acid resistance, and heat resistance. ### Research Objectives This paper aims to experimentally study the physical and chemical changes of different binders and alkaline activators under accelerated carbonation conditions, in particular: 1. **Physical Properties**: including changes in compressive strength, pH value, and neutralization depth. 2. **Chemical Properties**: Analyze the changes in hydration products through XRD, TG - DTG, and 29Si MAS NMR. ### Experimental Methods - **Materials and Preparation**: Mortar and paste specimens were prepared using blast furnace slag (BFS), fly ash (FA), and their 1:1 mixture as binders, and sodium silicate (SS) and sodium hydroxide (SH) as alkaline activators. - **Testing Conditions**: After curing the specimens at 20°C and 60% relative humidity for 8 weeks, an accelerated carbonation test was carried out under the conditions of 5% CO2 concentration, 20°C, and 60% relative humidity. - **Testing Methods**: The physical and chemical properties of the specimens were evaluated by compression tests, XRD, TG - DTG, and 29Si MAS NMR methods. ### Main Findings - **Compressive Strength**: Different alkaline activators have a significant impact on the compressive strength of the specimens. For example, the compressive strength of specimens using sodium silicate as an activator decreased after accelerated carbonation, while specimens using sodium hydroxide showed different behaviors. - **Chemical Changes**: Through XRD and 29Si MAS NMR analysis, it was found that the C–(N)–A–S–H structure changed during the carbonation process, resulting in a decrease or increase in compressive strength. In conclusion, this study provides important experimental data for understanding the physical and chemical changes of alkali - activated cements under accelerated carbonation conditions, which is helpful for optimizing the formula and application of alkali - activated cements.