Abstract:Concrete facilities in the severe-cold areas of western China (salt lake environments and heavy saline soils) are seriously damaged by the multiple corrosion effects of freeze–thaw cycles and sulfate corrosion. Magnesium phosphate cement (MPC) cement-based material has become an ideal concrete structural component because of its superior performance. Because concrete structural repair materials are used in heavy-corrosion environments, their durability in those environments should also be considered. Regarding the salt-freezing resistance of MPC, the existing studies have all used a NaCl solution as the heat transfer medium. In addition to chlorine salt, sulfate, especially Na2SO4, is also common in typical use environments such as oceans, salt lakes, and groundwater. To evaluate the sulfate freeze–thaw resistance of potassium magnesium phosphate cement (MKPC) mortar, in this study the strength development, weight loss, and water absorption of MKPC mortar specimens subjected to different freeze–thaw cycles were tested and compared with those for Portland cement (P.O) mortar specimens of the same strength grade. The results showed that the P.O mortar specimen completely lost its strength after 75 cycles of rapid water freezing and thawing and 50 cycles of sodium sulfate solution (5%) freezing and thawing. However, the residual strength rating of the MKPC mortar specimen after 75 cycles of water freezing and thawing and 100 cycles of sodium sulfate solution freezing and thawing was higher than 75%. After 50 rapid freeze–thaw cycles in water and a 5% Na2SO4 solution, the P.O mortar specimen’s mass loss exceeded the 5% failure standard, whereas the mass loss of the MKPC mortar specimens was much less than 5%. Before the freeze–thaw cycles, the water absorption of the P.O mortar specimen was close to 8 times that of the MKPC mortar specimen, and after 50 water freeze–thaw cycles and 25 sulfate solution freeze–thaw cycles, the water absorption reached 4.88% and 5.68%, respectively. However, after 225 freeze–thaw cycles in water and the sulfate solution, the water absorption rates of MKPC mortar specimens were 2.91% and 2.51% respectively. The test and analysis results show that the freeze–thaw resistance of MKPC mortar was much higher than that of Portland cement mortar specimens. Those results provide a prerequisite for applying and expanding the use of MKPC-based materials in severe-cold areas of western China (salt lake and heavily saline soil environments).

Durability of Magnesium Potassium Phosphate Cements (MKPCs) under Chemical Attack

Inorganic Acid Resistance Performances of Magnesium Phosphate Cement: A Two-Year Observation

Experimental Study of Magnesium Phosphate Cements Modified by Metakaolin

Chemical degradation of magnesium potassium phosphate cement pastes during leaching by demineralized water: Experimental investigation and modeling

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

Sulfuric Acid-Resistance Performances of Magnesium Phosphate Cements: Macro-properties, Mineralogy and Microstructure Evolutions

Microstructure of Magnesium Potassium Phosphate Cement

Experimental Study of Phosphate Salts Influencing Properties of Magnesium Phosphate Cement

Magnesium Potassium Phosphate Cement-Based Derivatives for Construction Use: Experimental Assessment

Microstructure and micromechanical properties of magnesium phosphate cement

Water-resisting Performances and Mechanisms of Magnesium Phosphate Cement Mortars Comprising with Fly-Ash and Silica Fume

Sulfate Freeze–Thaw Resistance of Magnesium Potassium Phosphate Cement Mortar

Hydration properties of magnesium phosphate cement paste mixed with metakaolin and silica fume

Properties of Magnesium Phosphate Cement Containing Steel Slag Powder

Calcium silicate cements endowing bioactivity and sustaining mechanical strength of low-heat-releasing and fast-curing magnesium phosphate cements

Hydration Products and Microstructural Properties Analysis of Magnesium Phosphate Cement Comprising with Industrial Residues

Engineering Properties and Microstructure Analysis of Magnesium Phosphate Cement Mortar Containing Bentonite Clay

Experimental evaluation of salt corrosion resistance of potassium salt magnesium phosphate cement coating slurry

Radiation stability and durability of magnesium phosphate cement for radioactive reactive metals encapsulation

Study on Bonding Performance of Magnesium Phosphate Cement Mortar in Chloride Corrosion Environment

Properties of Magnesium Phosphate Cement Containing Redispersible Polymer Powder