Abstract:The fine-grained tungsten heavy alloys (WHAs) with grain size of about 1-3 mu m were successfully prepared by spark plasma sintered W-7Ni-3Fe composite powders with different high-energy ball milling (HEBM) time. This study analyzes the effects of HEBM time not only on the composite powders but on the microstructure and mechanical properties of WHAs. The scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to investigate the microstructure and phase evolution rules of powders and alloys, respectively. The gamma-(Ni, Fe, W) is not observed in XRD patterns of the ball milled powders. With prolonging HEBM time, the W phase diffraction peak becomes increasingly wider, and its intensity continues to decline. However, the completely amorphous structures are not formed even after HEBM 40 h. The relative density of the WHAs prepared by HEBM assisted SPS technique decreases gradually with increasing the ball milling time. For the WHAs sintered in 1150 degrees C for 8 min, the W grains grow finer and the content of the gamma-(Ni, Fe, W) binding phase greatly increases with prolonging the HEBM time. Meanwhile, over 5 h of HEBM time, the bending strength continuously decreases and the hardness slightly increases. The intergranular fracture of the W grains is the main bending fracture mode in all the WHAs. The microporous of different sizes are distributed on the bending fracture and progressively increased with prolonging the ball milling time. (C) 2013 Elsevier B.V. All rights reserved.

Microstructure Characterization of W-Ni-Fe Heavy Alloys with Optimized Metallographic Preparation Method

Theoretical and experimental investigation of chemical mechanical polishing of W–Ni–Fe alloy

Microstructure and mechanical characterizations of liquid phase sintered W-Ni-Cu heavy alloy modified with La 2 O 3 and Fe addition

Fabrication, characterization, and mechanical properties of 93W–4.9Ni–2.1Fe/95W–2.8Ni–1.2Fe–1Al 2 O 3 heavy alloy composites

Investigation on grinding of tungsten heavy alloy with the assistance of electrochemical modification

Modification Of Tungsten Heavy Alloy By Selective Electrochemical Etching In Sodium Carbonate Electrolyte

Investigation on Preparation of Nanoporous Arrays of NiAl-W

Preparation of Fine-Grained Tungsten Heavy Alloys by Spark Plasma Sintered W–7Ni–3Fe Composite Powders with Different Ball Milling Time

Microstructure and Mechanical Properties of W-ZrO2 Alloys by Different Preparation Techniques

Microstructure and properties of tungsten heavy alloy by hot extrusion

Effect of Microalloying Addition on Microstructure and Mechanical Properties of Ni-W Coatings

Study on synthesis and structure of mechanically alloyed W-Ni-Fe nanocomposite powders

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Preparing Process of Fine-Grain Tungsten Heavy Alloy with High Mechanical Properties

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition

Densification, microstructural evolutions of 90W-7Ni-3Fe tungsten heavy alloys during laser melting deposition process

A Study about Fe-Ni Mechanical Alloying Process by Dry and Wet Method

Mechanical alloying of ODS tungsten heavy alloys and microstructure development of intermetallic compounds

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Microstructure and Properties of Ultra-Fine Tungsten Heavy Alloys Prepared by Mechanical Alloying and Electric Current Activated Sintering

Effect of Microstructure Refinement on Surface Morphology and Dynamic Mechanical Properties of W-Cu Alloys