Abstract:In this study, to obtain tungsten heavy alloy (WHA, 93W-4.9Ni-2.1Fe) with fine grain, high density and enhanced strength, W–Ni–Fe nanocomposite powder with high sintering driving force and small composite scale was designed and prepared. The effects of sintering temperature on the microstructure and properties of WHAs were systematically investigated. At a relatively low temperature of 1300 °C, WHAs with both high relative density of 98.0±0.31% and fine grain size of 2.07 μm were obtained, which was much smaller than that of traditional WHAs (30–60 μm). This special microstructure made it simultaneously achieve excellent compressive yield strength (1555 MPa), high strain-to-failure (over 40%) and hardness (480 HV0.5). This ultrahigh yield strength was about 2 times as the conventional WHAs with lager grain size. With the further increase of temperature to 1450 °C, the grain size of W grew significantly from 2.07 to 6.57 μm and the yield strength decreased remarkedly to 947 MPa. It was found that the W phase had good interfacial bonding with the γ-(Ni, Fe) matrix phase and the enhanced mechanical properties were mainly contributed by the small grain size and high ratio of phase boundary, which can significantly improve the storage capacity of dislocation.

Preparing Process of Fine-Grain Tungsten Heavy Alloy with High Mechanical Properties

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Microstructure and properties of liquid-phase sintered tungsten heavy alloys by using ultra-fine tungsten powders

Study on synthesis and structure of mechanically alloyed W-Ni-Fe nanocomposite powders

Phase transformation and thermal stability of mechanically alloyed W–Ni–Fe composite materials

Effect of Nanocrystalline Tungsten Powders on the Microstructure and Properties of Liquid-Phase Sintered 93W Alloys

Densification, Microstructure And Properties Of 90w-7ni-3fe Fabricated By Selective Laser Melting

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Mechanical alloying of ODS tungsten heavy alloys and microstructure development of intermetallic compounds

Tungsten heavy alloy: Nano-crystallinity and alloying induced low temperature sintering, microstructure and mechanical properties

Fine-grained 93W-4.9Ni-2.1Fe alloy with ultrahigh yield strength prepared via low temperature sintering of W nanocomposite powder

The effect of fine W particles in matrix phase on mechanical properties of tungsten heavy alloys

Preparation and Sintering Performance of W-Ni/Yb2O3 Composite Materials

The sintering of tungsten heavy alloy by mechanical alloying

Microstructure and mechanical properties of high density tungsten alloy and its influence factors

The simultaneous improvement of strength and ductility of the 93W-4.6Ni-2.4Fe prepared by additive manufacturing via optimizing sintering post-treatment

Microstructure Evolution and Mechanical Properties of Ultra-Fine Grain AlCrFe2Ni2Wx High-Entropy Alloys

Tem Characterization of the Microstructure of Hot-Hydrostatically Extruded 93W-4.9Ni-2.1fe Alloy

Effect of Y2O3 Addition on the Microstructure, Wear Resistance, and Corrosion Behavior of W-4.9Ni-2.1Fe Heavy Alloy

Microstructure and Mechanical Properties of a Hot-Hydrostatically Extruded 93w–4.9ni–2.1fe Alloy