Abstract:In this work, nanocrystalline W–Al alloys (up to 20 at.% of Al) were produced by high energy ball milling and powder microstructural evolution was investigated as a function of milling time. It was found that, regardless of the composition, alloys crystallite size progressively decreases and stabilizes around a value of about 10–15 nm after 70–100 h of mechanical treatment. The aluminum dissolution into the bcc W lattice was confirmed by DSC, SEM, and TEM. The formation of intermetallic compounds was detected neither during ball milling nor after thermal treatments up to 1450 °C. Sintering behavior of mechanically alloyed W–Al alloys was tested under pressureless conditions, and a significant improvement in terms of sinterability with respect to pure W was observed. Along with favoring the sintering process, the addition of Al also resulted in a notable enhancement of the coarsening resistance. Indeed, the analysis of ball-milled pure tungsten after thermal treatment at 1450 °C provided an estimated average crystallite size of about 2 μm, while W80Al20 and W90Al10 alloys retained an average crystallite size of about 70 nm and 60 nm, respectively. Although further work is required to optimize sintering conditions for achieving full density samples, the retaining of the nanostructure marks a significant advancement in the field of W-based alloys.

Study on synthesis and structure of mechanically alloyed W-Ni-Fe nanocomposite powders

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Studies on thermodynamic and kinetic and phase evolution of W-Ni-Fe powder during mechanical alloying

Phase transformation and thermal stability of mechanically alloyed W–Ni–Fe composite materials

The Morphology and Microstructure of Nanocrystalline Fe1-x-Nix Alloy Powders by Mechanical Alloying

Formation of Crystalline and Amorphous Solid Solutions of W–Ni–Fe Powder During Mechanical Alloying

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Comparative study of the microstructure and phase evolution of FeCoCrNiAl high-entropy alloy-matrix WC nanocomposite powders prepared by mechanical alloying

The Effect of Mechanical Alloying Technology on Microstrcture of Fe-Ni Alloy

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Preparation of Cbnp/Nicral Nanostructured Composite Powders by A Step-Fashion Mechanical Alloying Process

Nanocrystalline Ni-30wt%Fe Supersaturated Solid Solution Synthesized by Mechanical Alloying

Nanocrystalline and ultrafine grained materials by mechanical alloying

Effect of Milling Intensity on Structural Changes of Mixed Al-Fe-Ni Powders in Mechanical Alloying Process

Mechanical alloying of ODS tungsten heavy alloys and microstructure development of intermetallic compounds

Promoting the High Load-Carrying Capability of Al–20 Wt%sn Bearing Alloys Through Creating Nanocomposite Structure by Mechanical Alloying

Magnetic properties and Structural characterization of nanocrystalline Fe-20%A (Ni, Co and Si) alloys powders synthesized by mechanical alloying process

Different Cr contents in nanostructured Fe-Ni-Cr alloys prepared by Mechanical Alloying

Research of nanocrystalline Ni-30%Fe solid solution synthesized by mechanical milling