The Effect of Mechanical Alloying Technology on Microstrcture of Fe-Ni Alloy

刘奇正,孟庆平,戎咏华,徐祖耀

DOI: https://doi.org/10.3321/j.issn:1006-2467.2004.10.019

2004-01-01

Abstract:Fe-Ni nanocrystals with different Ni content were produced by mechanical alloying method through different milling time. X-ray diffraction (XRD) analysis indicated that in the samples with Ni content of 10% and 20%, Ni atoms entirely dissolved in the Fe lattice, and single α (bcc) phase forms after milling 20 h and 50 h respectively, while in the sample with 50% Ni, single γ (fcc) phase forms after milling 120 h, and the forward and backward transformations of γ (fcc) α (bcc) occur in turn. The solubilities of α (bcc) and γ (fcc) phase are obviously higher than those of their equilibrium conditions. The ( α (bcc)) and γ (fcc) phases in samples with 35% coexists during the whole milling time. Three XRD analysis methods were used to precisely measure grain size and microstrain, from which it was found that the grain sizes of Fe-Ni alloys with different Ni content reach nanometer range after milling 20 h, moreover, the grain size decreases and microstrain increases with prolonging milling time.