The Morphology and Microstructure of Nanocrystalline Fe1-x-Nix Alloy Powders by Mechanical Alloying

WANG Jinhui,ZHu Ruyang,CHEN Yunhong,WANG Jian,DU Youwei

DOI: https://doi.org/10.3321/j.issn:1001-9731.2000.01.015

2000-01-01

Abstract:Fe 1- x Ni x nanocrystalline powders were prepared by mechanical alloying,x is nominally 0.15,0.45,0.80 and milling time is 2,4,8,16,40 hours,respectively.SEM and XRD were employed to study the morphology and microstructure.It is found that the process of ball milling can be divided into three stages.At the early stage,element Fe and Ni particles form some large composite particles due to cold welding,at intermediate stage,the strain reach maximum value,and the composite particles rupture,the range of size become narrower,at last stage,Fe,Ni powders have completely alloyed and size builds up.Layer structure has been observed at 40h.As-milled sample(x =0.15) forms b.c.c.structure after 40h,whereas the samples (x =0.45 and 0.80) form f.c.c. structure at 40 and 16h,alternatively.As for x =0.45,the average grain size is 10nm or so after 40h milling,and the internal strain reach maximum value 0.76% at 16h.In the whole time,the deviation of Ni content is less than 3 at %.