A Study of the Crystallographic Pitting Behavior of Al-0.54Mg-0.66Si Aluminum Alloy in Acidic Chloride Solutions

Mingyang Chen,Yunlai Deng,Jianguo Tang,Shitong Fan,Xinming Zhang
DOI: https://doi.org/10.1016/j.matchar.2018.12.024
IF: 4.537
2019-01-01
Materials Characterization
Abstract:Some specific corrosion environments require Al-Mg-Si aluminum alloy extrusions to have superior corrosion resistance. In order to clarify its corrosion mechanism and enhance its corrosion resistance, the corrosion occurrence, propagation path and corrosion morphology of the alloy was characterized by scanning electron microscope (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). It was found that the corrosion of the alloy first occurred at the grain boundary. Then the grain boundary becomes the origin of the crystallographic pitting after being attacked, and Mg in the Mg5Si6 phase inside the grain is preferentially corroded by precipitate free zone (PFZ), so that the corrosion propagates into the interior of the grain. The morphology of crystallographic pitting presents a regular step-like planes and is always propagated parallel to the direction of {100}Al in the grain. Further, the corroded Mg5Si6 precipitates becomes cathodes in the local area at a later stage, leading to the regular step-like planes has been transformed into dimple-like appearances.
What problem does this paper attempt to address?