Abstract:In this study, ultrafine HfB 2 powders with low oxygen were synthesized by a flocculating settling process which yielded ceramic precursors and subsequent carbo/borothermal reduction of the precursors. The liquid phase precursor method can achieve uniform mixing of components at the molecular level through multiple complexation reactions, and then realize the carbo/borothermal reduction reaction at a lower temperature to obtain ultrapure HfB 2 powders. The as-resulted quasi-spherical HfB 2 powders under the optimum conditions (atomic molar ratio M:B:C = 1:2.8:10) calcined at 1500 & DEG;C for 1 h have an average particle size of 205 nm and an oxygen content of 0.097 wt.%. Detailed analysis of the phase evolution of precursors shows that the formation of HfB 2 particles is a mass diffusion mode from the external to internal HfO 2 cores. We reveal that below 1300 & DEG;C, HfC is not an intermediate product of HfB 2 powder during the transition of precursors. Instead, HfC was formed as a by-product at high temperatures in the carbo/borothermal reduction process. The proposed formation mechanism of HfB 2 is completely different from the traditional two-step transformation method. After the sintering of the ultrafine powders, the HfB 2 ceramics show a relative density of 96.1% and superior mechanical properties compared to other works. Furthermore, by simply replacing the initial metal source, chlorinated group IV and V transitional metals (Ti, Zr, Ta, Nb) can also convert into high-purity and ultrafine diborides. This work shows that flocculating settling assisted carbo/borothermal reduction has potential in lot size production of various high-purity and ultrafine boride powders.& COPY; 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Molten Salt Synthesis, Characterization, and Formation Mechanism of Superfine (hfxzr1‐x)b2 Solid‐solution Powders

Molten Salt Synthesis, Formation Mechanism, and Oxidation Behavior of Nanocrystalline HfB 2 Powders

Synthesis of Ti0.2Zr0.8B2 Solid‐solution Nanopowders by Molten Salt Assisted Borothermal Reduction

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Synthesis of superfine high-entropy metal diboride powders

Molten Salt Synthesis of Bismuth Ferrite Nano‐ and Microcrystals and Their Structural Characterization

Molten salt synthesis of ZnNb2O6 powder

Synthesis and Characterization of the Ternary Metal Diboride Solid‐solution Nanopowders

Synthesis of ZnO Nano-crystal Powder by Molten Salt Method

The Forming Mechanism and Thermal Stability of W-Zr Super-Saturated Solid Solution Powder Prepared by Mechanical Alloying

Synthesis of ZnNb2O6 powder with rod-like particle morphologies

Effects of ZnCl2 addition on the ZnNb2O6 powder synthesis through molten salt method

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

Synthesis of the superfine high-entropy zirconate nanopowders by polymerized complex method

Fabrication of High‐purity HfSi2 Powder Via Molten Salt‐assisted Magnesium Thermal Reduction

Effect of Raw Material Particle Size on the Synthesis of La 2 Zr 2 O 7 by the Molten Salt Method

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Synthesis of High‐entropy Diboride Nanopowders Via Molten Salt‐mediated Magnesiothermic Reduction

Synthesis and Formation Mechanism of HfB2 Ultrafine Powders with Low Oxygen Via Flocculating Settling Assisted Process and Carbo/borothermal Reduction

Synthesis of zirconium boride (ZrB2) rod crystals through salt-assisted boro/carbothermal reduction