Abstract:In the present study, ZrB2 nanoparticles were synthesized using sol-gel method. Zirconium alkoxide was used as the source of zirconium and boric acid as the source of boron. The size of precursor nanoparticle was controlled using the pH parameter inside the sol, and the formation of primary nuclei of ZrB2 phase and their crystallized amount were investigated using the temperature parameter. To evaluate the mechanism of product formation during the sol-gel process, TEM, SEM, DTA/TG, RAMAN, XRD, FTIR, and DLS methods were used. DLS analysis showed that the size of precursor particle inside the sol at pH less than 5 was below 10 nm. Measurements of viscosity and zeta potential inside the sol showed that in the acidic range, the particle stability decreases with increasing pH. Mixing of precursor particles at molecular level inside the sol was one of the important reasons in reducing the synthesis temperature of ZrB2 particles. FTIR analysis on chemical bonds showed that Zr-O-B bond was formed inside the gel powder. DTA analysis showed that the primary nuclei of ZrB2 particles were formed at a temperature of about 1400 °C. XRD observations proved that the primary nuclei of the ZrB2 phase crystallized and grew at a temperature of about 1500 °C. Surface research revealed that the specific surface area of the synthesized ZrB2 particles is equivalent to 115 m2/g, and also the surfaces of these particles are porous, and the size of these porosities is in meso range. SEM analysis showed that the particle size of ZrB2 having homogeneous morphology is about 50 nm. TEM microstructural analysis revealed that ZrB2 particles were formed uniformly and orderly in very fine dimensions.Graphical abstract

Effect of Raw Material Particle Size on the Synthesis of La 2 Zr 2 O 7 by the Molten Salt Method

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Synthesis of Ti0.2Zr0.8B2 Solid‐solution Nanopowders by Molten Salt Assisted Borothermal Reduction

Synthesis of ZnO Nano-crystal Powder by Molten Salt Method

Molten Salt Synthesis, Characterization, and Formation Mechanism of Superfine (hfxzr1‐x)b2 Solid‐solution Powders

Effect of Particle Size on Phase Structure of Zro2 Produced by Hydrolysis of Zrocl2 Solution

Molten salt synthesis of ZnNb2O6 powder

Preparation of Zirconia Powders by Sol-gel Process

Synthesis of ZnNb2O6 powder with rod-like particle morphologies

Effects of ZnCl2 addition on the ZnNb2O6 powder synthesis through molten salt method

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Molten Salt Synthesis of Lead Lanthanum Zirconate Titanate Stannate Powders and Ceramics

Supercritical Hydrothermal Synthesis of Nano-Zro2: Influence of Technological Parameters and Mechanism

Effects of Preparing Conditions on the Synthesis of Y2SiO5 Nanoparticles by Low-Temperature Molten Salt Method

Synthesis of complex niobate nanostructures via molten-salt reaction: Effect of ZrO 2 on product morphology

Synthesis of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 powders through the molten salt method

Improvement of ZrB2 nanopowder synthesis by sol-gel method via zirconium alkoxide/boric acid precursors

Synthesis, Densification and Characterization of Nanosized Oxide Ceramic Powders with Eutectic Compositions by Heating of Alcohol-Aqueous Salt Solutions

Investigation of the Process of Synthesizing ZrO2 Nanoparticles by Heating of Alcohol-Aqueous Salt Solutions