Abstract:Residual stress is a key factor affecting the properties of ceramic/metal brazed joints. In this work, the residual stress of sapphire/Ti6Al4V alloy joints brazed with CuTi+B composite filler after cooling and reheated to 400 °C was calculated by finite element numerical simulation method. The effect of the B content in the filler and the filler thickness on the residual stress distribution of brazed joints after cooling was studied. The results show that the residual stress is mainly concentrated in the area near the filler layer. The maximum von Mises stress is located in the filler layer and a large Z-axial (the direction perpendicular to the brazed surface) tensile stress is on the sapphire near the filler layer. The B content and the filler thickness have no significant effect on the distribution of residual stress, but they have a certain effect on the value of residual stress of the sapphire near the filler layer. The von Mises stress and the Z-axial stress of this area increase with the increase of B content, and they decrease first and then increases with the increase of filler thickness. When the sapphire/Ti6Al4V joint is reheated to 400 °C, its residual stress significantly reduces and the residual stress on the periphery of the filler layer changes from compressive stress to tensile stress. As the B content is 1 and 3 wt%, the sapphire/Ti6Al4V joint with a smaller residual stress can be obtained. The microstructure observation and shear tests of the joints show that cracks appear in the high stress concentration area and the fracture starts from the area with maximum axial tensile stress, which verifies the accuracy of the simulation results.

New Design of Sapphire Joints Brazed with Bismuth-Borate Glass

Novel design of sapphire/spinel transparent ceramic joints with double glass interlayers by coating and bonding

Joining high volume fraction SiC particle reinforced aluminum matrix composites using Bi2O3-B2O3-ZnO-BaO-Na2O glass

Effect of Borosilicate Glass on the Mechanical and Biodegradation Properties of 45S5-Derived Bioactive Glass-Ceramics

Microstructure evolution and mechanical properties of YAG/YAG joint using bismuth-borate glass

Improvement of microstructure and mechanical properties of Sapphire/Kovar alloy joints brazed with Ag-Cu-Ti composite filler by adding B powders

Sapphire joining using Ag70.5Cu27.5Ti2 brazing filler metal

Microstructure and Mechanical Property of Titanium Film-Modified Sapphire/High Nb-TiAl Alloy Joints Using Ag-Cu Filler by Vacuum Brazing

Joining of Sapphire and Hot Pressed Al2O3 Using Ag70.5Cu27.5Ti2 Brazing Filler Metal

Two-step joining of reaction bonded silicon carbide (RBSC) using borosilicate glass

Heterogeneous material joining of sapphire and TC4 alloy with a functionally graded interface

Preparation and Characterization of Low Temperature Heat-Treated 45S5 Bioactive Glass-Ceramic Analogues

Crystallization of ZABS glass and its wettability on diamond abrasive

Pressure-less joining of SiCf/SiC composites by Y2O3–Al2O3–SiO2 glass: Microstructure and properties

Joining MgAl2O4 ceramics using ZnO–Al2O3–SiO2 glass ceramic with precipitated ZnAl2O4

Interfacial evolution mechanism of MgAl2O4/MgAl2O4 joints bonded with lanthanum glass

Microstructures and properties of (65-x)SiO2-xBi2O3-10B2O3-25CuO glasses

Effects of surface roughness on the microstructure and mechanical properties of dissimilar sapphire/Invar36 alloy joints made by ultrashort pulsed laser micro-welding

Microstructure, mechanical and optical properties of MgAl2O4/MgAl2O4 joints bonded using CaO-Al2O3-SiO2 glass filler

Residual Stress Distribution in Sapphire/Ti6Al4V Alloy Joints Brazed with CuTi+B Composite Fillers

Kinetics of Interfacial Reaction Between Borosilicate Glass and Sapphire Substrate