Effect of Borosilicate Glass on the Mechanical and Biodegradation Properties of 45S5-Derived Bioactive Glass-Ceramics

Sanzhong Xu,Xianyan Yang,Xiaoyi Chen,Huifeng Shao,Yong He,Lei Zhang,Guojing Yang,Zhongru Gou

DOI: https://doi.org/10.1016/j.jnoncrysol.2014.09.002

IF: 4.458

2014-01-01

Journal of Non-Crystalline Solids

Abstract:The low mechanical reliability of bioactive glasses (BGs) is a critical limitation in hard tissue prosthetics. Herein, the effect of sol–gel-derived calcium borosilicate system (CBS) with low-melting temperature on the mechanical properties and biodegradation of 45S5 BG-derived bioactive glass-ceramics (BGC) was investigated. The 45S5 BG-based BGCs with 0–20% CBS content were fabricated via sintering treatment at 700–1100°C. The results confirmed that the sintering temperature range of 850–900°C for the 10% CBS-containing BGC (45S5/CBS10) exhibited higher compressive strength than those treated at either lower or higher temperature, and the strength was almost 2.5–3.0-fold higher than that of the pure 45S5 BGC. The 45S5/CBS10 BGCs fabricated at 850–900°C showed excellent biodegradation and bioactivity when soaking in Tris buffer and simulated body fluid, while the compressive strength only decreased slightly. Specifically, the 45S5/CBS10 scaffolds with a porosity of ~70% showed ~8.0MPa in compressive strength, which is comparable to the compressive values of human trabecular bone. It is, therefore, believed that the sol–gel-derived CBS is suitable for reinforcing the melt-derived BG and is helpful for developing low-temperature sintering BGC porous biomaterials because of their integration in appreciable biodegradation and reasonable mechanical properties.