Abstract:The microstructure of BaTiO3 (BT) nanocrystals was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), selected area electron diffraction (SAED), and (high-resolution) transmission electron microscopy [(HR)TEM]. The BT nanocrystals have a cubic perovskite structure as revealed by XRD and SAED. They were prepared by a hydrothermal method using different starting materials: (i) Using as-prepared titanium hydroxide and barium hydroxide as starting materials, BT nanocrystals were obtained with a narrow size distribution and an average grain size of 65 nm, exhibiting a spherical particle morphology and smooth surfaces. These nanocrystals showed almost uniform contrast in TEM. HRTEM lattice fringe images indicate a rather uniform, perfect crystal structure. (ii) Using barium hydroxide and titanium dioxide (anatase) as starting materials, many coarse-faceted cubic nanocrystals and a small amount of spherical particle were observed, indicating a developed bimodal size distribution. Diffraction contrast variations across these particles indicate the presence of high strain in these BT particles. The strain is probably caused by the lattice defects like OH− ions and their compensation by cation vacancies. HRTEM images demonstrated that (1 0 0) and (1 1 0) surface facets are present on these particles. In addition they revealed the presence of very small-nucleated BT islands at the edges of the faceted particles.

Crystallization of Batio3 Thin Film at 140 Degrees C by Metalorganic Decomposition Hydrothermal Method Using Tio2 Precursor

Crystallization of BaTiO<sub>3</sub> Thin Films Prepared by Metalorganic Decomposition with Hydrothermal Treatment at 140°C

Crystallization of BaTiO3Thin Film at 140°C by Metalorganic Decomposition Hydrothermal Method Using Different Precursors

Low-temperature Crystallization of Metal Organic Decomposition BaTiO3 Thin Film by Hydrothermal Annealing

Low-temperature Preparation of BaTiO 3 Thin Film by MOD and Hydrothermal Treatment

A Very Low-Temperature Growth of Batio3 Thin Film by Hydrothermal Treatment Following Sol-Gel Coating at 200 Degree Celsius

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Hydrothermal preparation of BaTiO3 thin film on silicon

(111)-Oriented Batio3 Thin Films Hydrothermally Formed On Tio2/Si Substrate

In-situpreparation of Polycrystalline BaTiO3thin Films on Silicon by Hydrothermal Method

Preparation of Nano-Structured BaTiO3 Thin Film by Electrophoretic Deposition and Its Characterization

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Formation of BaTiO3 and PbTiO3 thin films under mild hydrothermal conditions

Hydrothermal BaTiO3 Thin Films on Ti‐Covered Silicon: Characterization and Growth Mechanism

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Highly Oriented Growth of PbTiO3 Ferroelectric Nanostructure Directed by Organic Molecules under Hydrothermal Condition

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

Phase transition of PbTiO3 polycrystalline thin film prepared by metalorganic chemical vapor deposition on yttrium stabilized zirconium

The Growth and Phase Transitions of Epitaxial Pb(Zr0.95ti0.05)O-3 Thin Films Prepared by Sputter Deposition Combined with Post-Annealing on Srtio3(1 0 0)

Stoichiometry control and structure evolution in hydrothermally derived (Ba,Sr)TiO3 films

BaTiO3 Nanocrystals: Hydrothermal Synthesis and Structural Characterization