Abstract:Commercially pure titanium specimens are subjected to three different treatments, and their bioactivity are evaluated by immersing the specimens in a simulated body fluid (SBF, Kokubo's recipe) for various periods up to 7 days, with particular attention being paid to the differences in apatite deposition between surfaces open to SBF and surfaces in contact with the container's bottom. The treatment with a H(2)O(2)/HCl solution at 80 degrees C for 30 min followed by heating at 400 degrees C for 1 h produces an anatase titania gel layer on the specimen surface. This gel layer deposits apatite both on the contact and on open surfaces, and apatite deposition ability does not change with pre-staking in distilled water. The treatment with a NaOH solution at 60 degrees C for 3 days produces a sodium titanate gel layer. This gel layer can deposit apatite only on the contact surface, and the apatite deposition ability is completely lost after 1 day of pre-staking in distilled water. It is concluded, therefore, that the bioactivity of the titania gel originates from the favorable structure of the gel itself while the bioactivity of the sodium titanate gel depends heavily on ion release from the gel. The third treatment, a simple heat treatment at 400 degrees C for 1 h, produces a dense (not porous) oxide layer on the specimen surface. The specimens can deposit apatite on the contact surface after only 3 days of staking in SBF, but they cannot deposit apatite on the open surface for up to 2 months of staking. The implications of such apatite deposition behavior have been discussed in relation to the environments of titanium implants in bone as well as to the methodology of the SBF staking experiment.

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

Bioactive Titania-Gel Layers Formed by Chemical Treatment of Ti Substrate with a H2O2/HCl Solution.

Bioactive treatment of titanium surface using a H2O2/HCl solution

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

Crystallization of Amorphous Titania Gel by Hot Water Aging and Induction of in Vitro Apatite Formation by Crystallized Titania

In vitro bioactivity of anatase film obtained by direct deposition from aqueous titanium tetrafluoride solutions

Low-temperature Deposition of Rutile Film on Biomaterials Substrates and Its Ability to Induce Apatite Deposition in Vitro

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

Nanocrystalline Titania Made From Interactions Of Ti With Hydrogen Peroxide Solutions Containing Tantalum Chloride

Influence of film thickness on in vitro bioactivity of thin anatase films produced through direct deposition from an aqueous titanium tetrafluoride solution

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution

In Vitro Evaluation on Bone-Bonding of Chemically Modified Titanium

Apatite Formation on Rutile and Anatase Layers Derived by Hydrolysis of Titanylsulfate in a Simulated Body Fluid

In vitro apatite formation on nano-crystalline titania layer aligned parallel to Ti6Al4V alloy substrates with sub-millimeter gap

Direct Deposition of A Rutile Layer on Polymer Substrates to Induce Bioactivity in Vitro

Effect of the Substrate Temperature on the Crystallization of TiO2 Films Prepared by DC Reactive Magnetron Sputtering

Soft Solution Approach to Prepare Crystalline Titania Films