Abstract:PURPOSE:Using sandblast, double acid-etching and H(2)O(2)/HCl solution treatment to establish a new implant surface, and to analyze the surface's morphology.METHODS:After being polished, sandblasted, cleaned, the titanium specimens were divided into six groups, i.e.A to F group. The specimens of group A were treated with low concentration of HF/HNO(3) solution, Group B was treated with low concentration of HF/HNO(3) solution and then H(2)SO(4)/HCl solution, Group C was treated after Group B and further with H(2)O(2)/HCl solution at 80degrees centigrade for 30 minutes, and subsequently heated at 400degrees centigrade for 1 hour. Group D was treated with high concentration of HF/HNO(3) solution, Group E was treated after Group D and then H(2)SO(4)/HCl solution, Group F was treated after E group and further with H(2)O(2)/HCl solution at 80degrees centigrade for 30 minutes, and subsequenty heated at 400degrees centigrade for 1 hour.RESULTS:The titanium surface sandblasted and ultrasonically cleaned exhibited a great deal of particles. The titanium plates treated with low concentration of HF/HNO(3) solution still had some particles, but there were much nano-holes on the titanium surface. The titanium plates treated with high concentration of HF/HNO(3) solution had no particles on the surface, but showed much micron-holes on the titanium surface. The titanium plates treated with H(2)SO(4)/HCl solution after HF/HNO(3) solution etching had all particles removed and got multilevel holes on the surface.The last H(2)O(2)/HCl method produced an anatase titania gel layer on the specimen surface.CONCLUSION:By altering the concentration of HF/HNO(3) solution, we could make different sizes of apertures on the titanium surface. Double acid-etching can remove all sandblasting particles embedded in titanium surfaces and form multilevel holes. The H(2)O(2)/HCl method can turn the rough non- crystallographic TiO(2) layer into the anatase titania gel layer.

Bioactive Titania-Gel Layers Formed by Chemical Treatment of Ti Substrate with a H2O2/HCl Solution.

Bioactive treatment of titanium surface using a H2O2/HCl solution

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Crystallization of Amorphous Titania Gel by Hot Water Aging and Induction of in Vitro Apatite Formation by Crystallized Titania

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

In vitro bioactivity of anatase film obtained by direct deposition from aqueous titanium tetrafluoride solutions

Nanocrystalline Titania Made From Interactions Of Ti With Hydrogen Peroxide Solutions Containing Tantalum Chloride

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

Apatite Formation on Rutile and Anatase Layers Derived by Hydrolysis of Titanylsulfate in a Simulated Body Fluid

Low-temperature Deposition of Rutile Film on Biomaterials Substrates and Its Ability to Induce Apatite Deposition in Vitro

Porous titania films prepared from interactions of titanium with hydrogen peroxide solution

Nanostructured positively charged bioactive TiO2 layer formed on Ti metal by NaOH, acid and heat treatments

Soft Solution Approach to Prepare Crystalline Titania Films

The Preparation of the Multilevel Holes and Analysis of the Pure Titanium Surface

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution