Abstract:Commercially pure titanium specimens are subjected to three different treatments, and their bioactivity are evaluated by immersing the specimens in a simulated body fluid (SBF, Kokubo's recipe) for various periods up to 7 days, with particular attention being paid to the differences in apatite deposition between surfaces open to SBF and surfaces in contact with the container's bottom. The treatment with a H(2)O(2)/HCl solution at 80 degrees C for 30 min followed by heating at 400 degrees C for 1 h produces an anatase titania gel layer on the specimen surface. This gel layer deposits apatite both on the contact and on open surfaces, and apatite deposition ability does not change with pre-staking in distilled water. The treatment with a NaOH solution at 60 degrees C for 3 days produces a sodium titanate gel layer. This gel layer can deposit apatite only on the contact surface, and the apatite deposition ability is completely lost after 1 day of pre-staking in distilled water. It is concluded, therefore, that the bioactivity of the titania gel originates from the favorable structure of the gel itself while the bioactivity of the sodium titanate gel depends heavily on ion release from the gel. The third treatment, a simple heat treatment at 400 degrees C for 1 h, produces a dense (not porous) oxide layer on the specimen surface. The specimens can deposit apatite on the contact surface after only 3 days of staking in SBF, but they cannot deposit apatite on the open surface for up to 2 months of staking. The implications of such apatite deposition behavior have been discussed in relation to the environments of titanium implants in bone as well as to the methodology of the SBF staking experiment.

Crystallization of Amorphous Titania Gel by Hot Water Aging and Induction of in Vitro Apatite Formation by Crystallized Titania

Bioactive treatment of titanium surface using a H2O2/HCl solution

Bioactive Titania-Gel Layers Formed by Chemical Treatment of Ti Substrate with a H2O2/HCl Solution.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

In vitro bioactivity of anatase film obtained by direct deposition from aqueous titanium tetrafluoride solutions

Low-temperature Deposition of Rutile Film on Biomaterials Substrates and Its Ability to Induce Apatite Deposition in Vitro

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

Apatite Formation on Rutile and Anatase Layers Derived by Hydrolysis of Titanylsulfate in a Simulated Body Fluid

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution

In Vitro Bioactivity of Hydrogen Peroxide Modified Titanium: Effects of Surface Morphology and Film Thickness

In Vitro Evaluation on Bone-Bonding of Chemically Modified Titanium

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Influence of film thickness on in vitro bioactivity of thin anatase films produced through direct deposition from an aqueous titanium tetrafluoride solution

In vitro apatite formation on nano-crystalline titania layer aligned parallel to Ti6Al4V alloy substrates with sub-millimeter gap

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].