Abstract:Commercially pure titanium specimens are subjected to three different treatments, and their bioactivity are evaluated by immersing the specimens in a simulated body fluid (SBF, Kokubo's recipe) for various periods up to 7 days, with particular attention being paid to the differences in apatite deposition between surfaces open to SBF and surfaces in contact with the container's bottom. The treatment with a H(2)O(2)/HCl solution at 80 degrees C for 30 min followed by heating at 400 degrees C for 1 h produces an anatase titania gel layer on the specimen surface. This gel layer deposits apatite both on the contact and on open surfaces, and apatite deposition ability does not change with pre-staking in distilled water. The treatment with a NaOH solution at 60 degrees C for 3 days produces a sodium titanate gel layer. This gel layer can deposit apatite only on the contact surface, and the apatite deposition ability is completely lost after 1 day of pre-staking in distilled water. It is concluded, therefore, that the bioactivity of the titania gel originates from the favorable structure of the gel itself while the bioactivity of the sodium titanate gel depends heavily on ion release from the gel. The third treatment, a simple heat treatment at 400 degrees C for 1 h, produces a dense (not porous) oxide layer on the specimen surface. The specimens can deposit apatite on the contact surface after only 3 days of staking in SBF, but they cannot deposit apatite on the open surface for up to 2 months of staking. The implications of such apatite deposition behavior have been discussed in relation to the environments of titanium implants in bone as well as to the methodology of the SBF staking experiment.

Low-temperature Deposition of Rutile Film on Biomaterials Substrates and Its Ability to Induce Apatite Deposition in Vitro

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

A Comparative Study of in Vitro Apatite Deposition on Heat-, H(2)O(2)-, and NaOH-treated Titanium Surfaces.

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

Direct Deposition of A Rutile Layer on Polymer Substrates to Induce Bioactivity in Vitro

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

In vitro bioactivity of anatase film obtained by direct deposition from aqueous titanium tetrafluoride solutions

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Influence of film thickness on in vitro bioactivity of thin anatase films produced through direct deposition from an aqueous titanium tetrafluoride solution

Apatite Formation on Rutile and Anatase Layers Derived by Hydrolysis of Titanylsulfate in a Simulated Body Fluid

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution

Bonelike Apatite Formation on Synthetic Organic Polymers and Fiber Coated with Titania

Crystallization of Amorphous Titania Gel by Hot Water Aging and Induction of in Vitro Apatite Formation by Crystallized Titania

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

In Vitro Bioactivity of Hydrogen Peroxide Modified Titanium: Effects of Surface Morphology and Film Thickness

Biomimetic Apatite Coatings on Micro-Arc Oxidized Titania

Preparation of Hydroxyapatite / Titania Double Layer Coating on Poly-I-lactide Due to Hydrolysis of Titanium Tetrachloride

Formation Mechanism of Biomedical Apatite Coatings on Porous Titania Layer

Preparation of Hierarchical Porous Structure on Ti Surface and Bioactivity