Abstract:Bioceramic hydroxyapatite/sodium titanate coating on sandblasted titanium substrate was fabricated by a three-step process. At first, the sandblasted titanium substrate was coated with a flake-like sodium titanate layer by alkali-heat treatment. In the second step, the alkali-heat treated titanium substrate was hydrothermal treated at 180 °C for 4 h with calcium solutions. In the third step, the hydroxyapatite (HA) coating was deposited onto the hydrothermal treated layer via electrochemical deposition method. The surface topography and roughness of the coatings were determined by field emission scanning electron microscope (FESEM) and a mechanical contact profilometer, respectively. The surface compositions were evaluated by X-ray diffraction (XRD), energy-dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). The EDS, XPS, and XRD analysis confirm the presence of element Ca, Ca2+, and CaTiO3 on sodium titanate layer after hydrothermal treatment with Ca(NO3)2 solution, respectively. FESEM micrograph shows the rod/needle-shaped crystallites are highly densely packed on the calcium-ion-containing layer with an average size of ~50 nm in diameter. The results indicate that the sodium titanate layer containing Ca2+ ions possesses higher ability to induce HA formation compared with the pure sodium titanate layer. It is revealed that surface composition plays an important role in the electrochemical deposition of HA. The calcium-ion-containing layer probably makes the nucleation of HA easy and effectively promotes orientated growth of HA on flake-like sodium titanate surface. The sodium titanate layer possesses a lower corrosion current density and a higher corrosion potential than sandblasted-Ti substrate. The sodium titanate layer should act as a barrier to the release of metal ions from metallic substrate to physiological solutions and thus reducing the electrochemical reaction rate.

Preparation of Hydroxyapatite / Titania Double Layer Coating on Poly-I-lactide Due to Hydrolysis of Titanium Tetrachloride

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Bioactive treatment of titanium surface using a H2O2/HCl solution

Bioactive Titania-Gel Layers Formed by Chemical Treatment of Ti Substrate with a H2O2/HCl Solution.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

A Novel Method to Synthesize Hydroxyapatite Coating with Hierarchical Structure

Direct Deposition of A Rutile Layer on Polymer Substrates to Induce Bioactivity in Vitro

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Low-temperature Deposition of Rutile Film on Biomaterials Substrates and Its Ability to Induce Apatite Deposition in Vitro

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Bonelike Apatite Formation on Synthetic Organic Polymers and Fiber Coated with Titania

In vivo and in vitro biological efficacy of double-layer coating of titanium with gelatin and calcium phosphate

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Fabrication and in vitro evaluation of the collagen/hyaluronic acid PEM coating crosslinked with functionalized RGD peptide on titanium.

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Preparation of Bioactive Hydroxyapatite on Pure Titanium

Preparation of Layered Bioceramic Hydroxyapatite/Sodium Titanate Coatings on Titanium Substrates Using A Hybrid Technique of Alkali-Heat Treatment and Electrochemical Deposition

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces

PREPARATION OF BIOACTIVE FILM ON Ti6Al4V