Abstract:For development of thin bioactive coatings on metal implants, a dense and uniform apatite layer was coated onto titanium (Ti) implants in situ by using a new biomimetic method, which is composed of apatite nucleation and growth steps in simulated body fluid (SBF). Analysis of the coatings by thin film X-ray diffraction and scanning electron microscopy-energy dispersive X-ray microanalysis (SEM-EMPA) before implantation showed that its characteristics were very similar to those of natural bone. The coated and uncoated rectangular plates were bilaterally implanted into the tibial proximal metaphyses of rabbits. After 6, 10 and 25 weeks post-implantation, the bone bonding and bone formation at the bone-implant interfaces were evaluated by a detachment test and undecalcified histological examination. Mechanical testing in tension showed that the failure load of apatite layer-coated Ti implants was significantly higher than that of uncoated control at each time period (all P < 0.001). Histologically, it was shown that bone was deposited directly onto the apatite coating without any intervening soft tissue, while in the paired controls, interpositional soft tissue was seen at the bone-implant interface. By SEM-EPMA, a uniform calcium- and phosphorus-rich layer was detected between the coated implants and bone, but not in uncoated controls at either earlier or later time periods. The results indicate that the apatite layer deposited on Ti in situ may significantly increase the bone bonding strength by providing a bioactive surface, which allows for an early bone apposition to the implant. In addition, the apatite layer-coated Ti produced by the biomimetic process may fulfil the requirements of favourable thin coatings and strong adhesion at the metal-coating interface.

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H(2)O(2)-, and NaOH-treated Titanium Surfaces.

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Low-temperature Deposition of Rutile Film on Biomaterials Substrates and Its Ability to Induce Apatite Deposition in Vitro

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces

Low-Temperature Deposition of Bioactive Crystalline Titania Films: Effects of Tantalum

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Formation Mechanism of Biomedical Apatite Coatings on Porous Titania Layer

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

BIOCERAMIC COATINGS ON TITANIUM SURFACES

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

In vitro bioactivity of anatase film obtained by direct deposition from aqueous titanium tetrafluoride solutions

Biomimetic Deposition of Apatite Coatings on Biomedical Niti Alloy Coated with Amorphous Titanium Oxide by Microarc Oxidation

The Biomimetic Deposition of Carbonate Apatite Induced by Titanium Base Calcium Enriched Silica Films

Crystallization of Amorphous Titania Gel by Hot Water Aging and Induction of in Vitro Apatite Formation by Crystallized Titania

Biomimetic Apatite Coatings on Micro-Arc Oxidized Titania

Apatite Formation Induced by Alkaline Treatment on Titanium Alloy Substrate