Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Wq Yan,K Kawanabe,T Nakamura,T Kokubo

DOI: https://doi.org/10.1016/B978-008042692-1/50109-6

1997-01-01

Abstract:The objective of this study was the development and use of a biomimetic coating method, which deposits a thin and uniform apatite layer onto titanium (Ti) implants in simulated body fluid (SBF), for improving their bone-bonding ability. The mechanical characteristics and histology of commercially pure Ti and apatite layer-coated Ti-6Al-4V alloy were investigated in rabbit tibiae. Interface failure load was determined using a detaching test after periods of 6, 10, 24, and 32 weeks. The apatite layer-coated implants exhibited significantly higher failure load than the uncoated control at each time period (all p < 0.001). Histologically, the coated-implants bonded directly to bone via the uniform coating, with no intervening soft tissue. In uncoated controls, there was fibrous tissue intervening at the interface even at longer periods. SEM-EPMA demonstrated a Ca-P-rich layer on the coated implants and direct bonding at the interface. No sign of degradation and delamination of the coating was seen after periods of up to 32 weeks. Our results suggest that apatite layer coating on Ti alloys in situ may improve bone-to-implant bonding and make it as a promising coating material.