Abstract:BACKGROUND: Electrochemically deposited coating, as an alternative method of plasma spraying coating, has arose widely attention, however, few reports concerning its in vivo biological features, especially the effect of coating on early osseointegration and duration of bone healing is poorly understood. OBJECTIVE: To investigate the early osseointegration of electrodepositied calcium phosphate and calcium phosphate/chitosan coatings on rabbits' femurs. DESIGN, TIME AND SETTING: An open experiment. The experiment was performed at the Key Laboratory for Oral Biomedical Engineering of Ministry of Education, Stomatology School of Wuhan University from April 2008 to May 2009. MATERIALS: Eighteen male Japanese rabbits were supplied by the animals' center of Wuhan University. Ti_6Al_4V alloy was purchased from Baoji Titanium Nickel Co., Ltd. Chitosan with over 75% degree of deacetylation was produced by American Sigma Company.METHODS: ① Cylindrical titanium alloy implants (3.3×8.0 mm) were designed with a gap (0.3×4.0 mm) in the middle part by using precision machine tool. The implants were prepared electrodeposited calcium phosphate coating surface (ELD group) and electrodeposited calcium phosphate/chitosan coating surface (ELDC group) with 2.5 mA/cm~2 electric current and 52 V temperature. Meantime, the implants with sandblasted surface were prepared as the control group. Totally 36 implants were randomly inserted into the distal femur condyles of 18 rabbits, and the new bone formation was labeled by fluorescence staining. MAIN OUTCOME MEASURES: At weeks 2 and 4 after operation, the implants were subjected to histological and histomorphometric analysis. RESULTS: All groups were observed different-quantity new bone formation. However, only ELDC group was seen fibrous tissues intervened at bone-to-implant interface. The ELD coatings were heterogeneously degraded, and the majority of the ELDC coatings were degraded. The new bone within gaps of ELD and control groups could be seen under the confocal laser scanning microscope with a continuous process of bone apposition. Percentages of bone-to-implant contact within and outside of the gaps of ELD group at weeks 2 and 4 were significantly higher than those of ELDC and control groups (P < 0.05). Bone formation rates of ELD group were significantly higher than those of ELDC group at weeks 2 and 4 after operation (P < 0.05). CONCLUSION: ELD implants can promote early osseointegration and induce bone tissue growth into the gaps; however, ELDC implants go against osseointegration of rabbit femurs.

In Vivo Comparison of Bone Formation on Titanium Implant Surfaces Coated with Biomimetically Deposited Calcium Phosphate or Electrochemically Deposited Hydroxyapatite

Biomechanical comparison of biomimetically and electrochemically deposited hydroxyapatite-coated porous titanium implants.

Effects of biomimetically and electrochemically deposited nano-hydroxyapatite coatings on osseointegration of porous titanium implants.

Bone Responses to Rough Titanium Implants Coated with Biomimetic Ca-P in Rabbit Tibia.

Biological and Biomechanical Behavior of Titanium Implants with Fluoridated Hydroxyapatite Coatings

Effects of magnesium-substituted nanohydroxyapatite coating on implant osseointegration.

[Analysis of Apposition on Differently Treated Implant Surface at Early Stage of Implantation].

Effect of Electrochemically Deposited Nanohydroxyapatite on Bone Bonding of Sandblasted/Dual Acid-Etched Titanium Implant

Effects of Zinc-Substituted Nano-Hydroxyapatite Coatings on Bone Integration with Implant Surfaces

Osteoblast Responses to Thin Nanohydroxyapatite Coated on Roughened Titanium Surfaces Deposited by an Electrochemical Process.

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Osteoblast Response to Porous Titanium Surfaces Coated with Zinc-Substituted Hydroxyapatite

Effect of Strontium-Substituted Nanohydroxyapatite Coating of Porous Implant Surfaces on Implant Osseointegration in a Rabbit Model.

Early Bone Apposition in Vivo on Plasma-Sprayed and Electrochemically Deposited Hydroxyapatite Coatings on Titanium Alloy.

The analysis of the bone response to the different treated implant surfaces at early stage of implantation

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

Promotion of Osteogenic Differentiation of Stem Cells and Increase of Bone-Bonding Ability in Vivo Using Urease-Treated Titanium Coated with Calcium Phosphate and Gelatin

Electrochemical Deposition of Nanostructured Hydroxyapatite Coating on Titanium with Enhanced Early Stage Osteogenic Activity and Osseointegration

Early osseointegration of electrodeposited calcium phosphate coatings on rabbits'femurs

The morphological effect of nanostructured hydroxyapatite coatings on the osteoinduction and osteogenic capacity of porous titanium

In vivo osseointegration evaluation of implants coated with nanostructured hydroxyapatite in low density bone