Highly Oriented Growth of PbTiO3 Ferroelectric Nanostructure Directed by Organic Molecules under Hydrothermal Condition

YIN Si-min,REN Zhao-hui,CHAO Chun-ying,XIAO Zhen,LIU Zhen-ya,SHEN Ge,HAN Gao-rong

DOI: https://doi.org/10.3969/j.1000-6281.2013.01.007

2013-01-01

Abstract:Four organic molecules including ethyl alcohol,oleic acid,oleylamine and poly acrylic acid have been introduced into a hydrothermal process to modify the crystal growth of perovskite lead titanate(PbTiO3,PT) nanostructures.The resulting products were systematically characterized by using X-ray powder diffraction(XRD),scanning electron microscope(SEM),Raman scattering spectroscop,transmission electron microscope(TEM) and high-resolution TEM(HRTEM).Corresponding morphology of the samples changes from donut-like microplates,square nanoplates,broken cubes to aggregated nanoplates.The results indicated that the introduction of 10 mL ethyl alcohol was particularly favourable to form donut-like single-crystal microplates of PT with an average lateral length of about 5～20 μm and a thickness of about 150 nm.XRD,TEM and HRTEM results suggested that the donut-like single-crystal microplates of PT probably experience a strong preferential growth along ab crystal planar via an oriented attachment mechanism.It is proposed that a selective absorbance of ethyl alcohol molecules on the {001} planes of tetragonal perovksite PT plays a key role in a preferred precipitation of crystal nucleates and thus the formation of donut-like microplates.