Self-Templated Synthesis of Single-Crystal and Single-Domain Ferroelectric Nanoplates
Chunying Chao,Zhaohui Ren,Yihan Zhu,Zhen Xiao,Zhenya Liu,Gang Xu,Jiangquan Mai,Xiang Li,Ge Shen,Gaorong Han
DOI: https://doi.org/10.1002/anie.201204792
2012-01-01
Abstract:Low-dimensional nanomaterials, such as nanowires and nanotubes, 3] have received extensive attention because of their fascinating catalysis, optics, and electronics 7] properties, which offer the opportunity to fabricate nanodevices. Much attention has been paid to materials with two-dimensional (2D) nanostructure because of their unique electronic, magnetic, and storage properties. In particular, the recent development of stable graphene has stimulated great interest in studying free-standing 2D nanomaterials. So far, a variety of 2D free-standing materials with nanostructure, such as PbS nanosheets, WO3 nanoplates, [10] CeO2 nanoplates, [11] MoS2 nanoflakes, 13] and TiO2 nanosheets, [4] have been successfully synthesized. Compared to these simple compounds, 2D free-standing, single-crystal multicomponent oxide nanomaterials, such as ferroelectric oxides, have been rarely reported because of the relatively complex crystal structures and rigid crystalline properties of these oxides. Ferroelectric oxide nanomaterials, such as PbTiO3 (PT), Pb(Zr,Ti)O3, and BaTiO3, have versatile properties for various technical applications ranging from nonvolatile ferroelectric random access memories (NFERAMs) to electromechanical applications. 15] Among these nanomaterials, 2D free-standing, single-crystal ferroelectric materials are highly attractive because of their potential performances. For example, ultrathin single crystals of BaTiO3 [16,17] prepared by focused ion beam (FIB) microscopy have been used as single-crystal capacitors with thicknesses down to about 65 nm. These ferroelectric platelets fabricated by FIB have greatly improved our understanding of the fundamental properties of thin films. However, recent theoretical research predicts that ferroelectric nanodiscs could even favor an ultimate NFERAM density of 60 10 bits per square inch as well as a new toroid moment. In contrast to the conventional properties, the surface chemistry of ferroelectric oxides only gradually became an active field of research. In particular, it has been predicted that CO and NO catalysis could be favored on ultrathin Pt(100) films supported on ferroelectric PbTiO3. [22] Various methods have so far been applied to fabricate 0D and 1D ferroelectric nanomaterials, including templated methods, sol-gel processing, 28] soft-chemistry routes, solvothermal/hydrothermal reactions, 31] and electrospinning techniques. 33] Despite much effort, there is still an absence of a simple wet-chemistry method to prepare 2D single-crystal ferroelectric nanomaterials, such as nanoplates and nanodiscs. Here we report, for the first time, that freestanding, single-crystal PT nanoplates can be synthesized by a facile hydrothermal method. The characterization of the microstructure by X-ray diffraction (XRD) and high-resolution transmussion electron microscopy (HRTEM) demonstrates that these PT nanoplates, with side lengths of 600– 1100 nm and heights of about 150 nm, grow along the ab plane of the tetragonal perovskite structure and that {001} facets at the top and bottom surfaces are exposed. The “self-templated” crystal growth has been employed to discuss the mechanism for the formation of PT nanoplates under hydrothermal conditions. Electrostatic force microscopy in the dynamic contact mode (DC-EFM) of operation was also used to study the ferroelectric properties of the PT nonaplates. Furthermore, the catalytic performance of the nanoplates for the oxidation of carbon monoxide (CO) has been evaluated. In brief, tetragonal-phase PT nanoplates were synthesized by a hydrothermal method at 200 8C by using 6m KOH. Figure 1a shows a typical XRD pattern (JCPDS 70-0746) of PT nanoplates prepared by the hydrothermal process at 200 8C for 12 h with 6m KOH, and indicates that the product has a pure tetragonal perovskite PT structure. More importantly, the intensity of the (001) diffraction peak is dramatically higher than that of (100), which is opposite to the case in conventional perovskite PT (JCPDS 70-0746). This observation reveals that {001} crystal planes are prevailent in the sample. Scanning electron microscopy (SEM) and TEM analysis show that the products consist of well-defined structures with a rectangular outline and a side length of 600–1100 nm (Figure 1b,c). The HRTEM image (Figure 1d) of a PT nanoplate shows a clear crystal lattice with uniform interplanar spacings of 0.390 nm and 0.390 nm, which correspond to the tetragonal (100) and (010) planes, respectively, and indicate that the PT nanoplates grow along the ab plane of the perovskite structure. The effect of the KOH concen[*] C. Y. Chao, Dr. Z. H. Ren, Z. Xiao, Z. Y. Liu, Dr. G. Xu, J. Q. Mai, Dr. X. Li, Dr. G. Shen, Dr. G. R. Han State Key Laboratory of Silicon Materials Department of Materials Science and Engineering Cyrus Tang Center for Sensor Materials and Application Zhejiang University, Hangzhou 310027 (P.R. China) E-mail: renzh@zju.edu.cn hgr@zju.edu.cn