Abstract:Adjustable-ring-mode laser welding (ARM-LW) offers a novel approach to minimize porosity in medium-thickness aluminum alloy joints. However, the suppression mechanism and optimization strategy of reducing porosity for ring-mode laser remain unclear. A combination of experiment and simulation was utilized to narrow the gap. The findings demonstrated that ring-mode laser effectively slows the increase of porosity with rising penetration depth compared to traditional Gaussian laser welding. The pore formation involves bubble generation induced by keyhole instability and bubbles being captured by the solidification front. As ring power share increases, the keyhole opening widens and becomes more stable, which enhances the energy absorption of keyhole walls, particularly in the bottom and middle sections. This enhances the keyhole stability and reduces bubble formation resulting from keyhole collapse. Additionally, as ring power share grows, a decrease of 63.2 % of -X-velocity suggests that bubbles are moving at a slower pace away from the keyhole bottom, increasing the chances of them being captured by keyhole and eventually vanishing; however, a decrease of 52.4 % of +Z-velocity raises the possibility of bubbles being trapped by solidification front if not caught by keyhole. Finally, a comprehensive discussion and analysis of how to mitigate porosity during ARM-LW are presented. A criterion—minimizing penetration to spot diameter ratio (PDR)—was proposed to guide ring power share selection. The insights into keyhole fluctuation and bubble evolution mechanisms outlined here can guide mitigating porosity in laser welding of medium-thickness aluminum alloy plates.

Experimental Investigation and Numerical Study on the Elimination of Porosity in Aluminum Alloy Laser Welding and Laser–GMA Welding

Numerical Study of Keyhole Instability and Porosity Formation Mechanism in Laser Welding of Aluminum Alloy and Steel

Numerical study of keyhole dynamics and porosity formation during high‐power oscillating laser welding of medium‐thick aluminum alloy plates

Investigation of the Inhibition Mechanism of Process Porosity in Laser-MIG Hybrid-Welded Joints for an Aluminum Alloy

Effect of Magnesium Content on Keyhole-Induced Porosity Formation and Distribution in Aluminum Alloys Laser Welding

Investigation on Porosity Suppression in Deep-Penetration Laser Welding by Using Computational Fluid Dynamics

Droplet Transfer Induced Keyhole Fluctuation and Its Influence Regulation on Porosity Rate during Hybrid Laser Arc Welding of Aluminum Alloys

Porosity inhibition of aluminum alloy by power-modulated laser welding and mechanism analysis

Modeling and numerical study of keyhole-induced porosity formation in laser beam oscillating welding of 5A06 aluminum alloy

Role of Welding Speed on Keyhole-Induced Porosity Formation Based on Experimental and Numerical Study in Fiber Laser Welding of Al Alloy

Keyhole-induced Pore Formation Mechanism in Laser-Mig Hybrid Welding of Aluminum Alloy Based on Experiment and Multiphase Numerical Model

Influence Of Arc Power On Keyhole-Induced Porosity In Laser Plus Gmaw Hybrid Welding Of Aluminum Alloy: Numerical And Experimental Studies

Investigation on the keyhole/molten pool dynamic behavior during adjustable ring-mode laser welding of medium-thick aluminum alloy

Mitigation of porosity in adjustable-ring-mode laser welding of medium-thick aluminum alloy

Porosity Sensitivity of A356 Al Alloy During Fiber Laser Welding

Study of Molten Pool Dynamics and Porosity Formation Mechanism in Full Penetration Fiber Laser Welding of Al-alloy

MECHANISMS OF THE POROSITY FORMATION DURING THE FIBER LASER LAP WELDING OF ALUMINIUM ALLOY

Relationship Between Molten Pool Behavior and Keyhole-Induced Porosity in Pulsed Laser-arc Hybrid Welding of Magnesium Alloy

Porosity in fiber laser formation of 5A06 aluminum alloy

Porosity Formation and Its Effect on the Properties of Hybrid Laser Welded Al Alloy Joints

Numerical study of keyhole-induced porosity suppression mechanism in laser welding with beam oscillation