Abstract:Adjustable-ring-mode laser welding (ARM-LW) offers a novel approach to minimize porosity in medium-thickness aluminum alloy joints. However, the suppression mechanism and optimization strategy of reducing porosity for ring-mode laser remain unclear. A combination of experiment and simulation was utilized to narrow the gap. The findings demonstrated that ring-mode laser effectively slows the increase of porosity with rising penetration depth compared to traditional Gaussian laser welding. The pore formation involves bubble generation induced by keyhole instability and bubbles being captured by the solidification front. As ring power share increases, the keyhole opening widens and becomes more stable, which enhances the energy absorption of keyhole walls, particularly in the bottom and middle sections. This enhances the keyhole stability and reduces bubble formation resulting from keyhole collapse. Additionally, as ring power share grows, a decrease of 63.2 % of -X-velocity suggests that bubbles are moving at a slower pace away from the keyhole bottom, increasing the chances of them being captured by keyhole and eventually vanishing; however, a decrease of 52.4 % of +Z-velocity raises the possibility of bubbles being trapped by solidification front if not caught by keyhole. Finally, a comprehensive discussion and analysis of how to mitigate porosity during ARM-LW are presented. A criterion—minimizing penetration to spot diameter ratio (PDR)—was proposed to guide ring power share selection. The insights into keyhole fluctuation and bubble evolution mechanisms outlined here can guide mitigating porosity in laser welding of medium-thickness aluminum alloy plates.

Porosity Formation and Its Effect on the Properties of Hybrid Laser Welded Al Alloy Joints

Effect of Porosity Morphology and Elements Characteristics on Mechanical Property in T-joints During Dual Laser-Beam Bilateral Synchronous Welding of 2060/2099 Al-Li Alloys

Investigation of the Inhibition Mechanism of Process Porosity in Laser-MIG Hybrid-Welded Joints for an Aluminum Alloy

Droplet Transfer Induced Keyhole Fluctuation and Its Influence Regulation on Porosity Rate during Hybrid Laser Arc Welding of Aluminum Alloys

Effect of swinging laser on porosity, microstructure, and mechanical properties of laser welded aluminum alloy joints with different lap forms

Porosity inhibition of aluminum alloy by power-modulated laser welding and mechanism analysis

Porosity morphology and its evolution mechanism in laser mirror welding of 2219 aluminum alloy

Formation Regularity of Pores During Laser Welding of Die-Cast Magnesium Alloys and Its Mechanism

Effect of filler materials on the porosity formation of aluminum alloy by laser welding with filler wire

Mechanical Characterization and Prediction of Aluminum Alloy Laser Welding Joints Including Roles of Geometries and Porosity

Mitigation of porosity in adjustable-ring-mode laser welding of medium-thick aluminum alloy

Porosity, Element Loss, and Strength Model on Softening Behavior of Hybrid Laser Arc Welded Al-Zn-Mg-Cu Alloy with Synchrotron Radiation Analysis

Microstructural Inhomogeneity in the Fusion Zone of Laser Welds

Reducing the Porosity in Die-Cast Magnesium Alloys During Laser Welding

Study on the influence of Al-Si welding wire on porosity sensitivity in laser welding and process optimization

Effects of Welding Parameters on Weld Porosity During CO2 Laser Welding of Die-Cast Magnesium Alloys

Experimental investigations on mechanical properties of AA6061-T6 aluminum alloy joined by laser welding using digital image correlation

Effect of ambient pressure on laser welding of AlSi10Mg fabricated by selected laser melting

Laser pressure welding of Al-Li alloy 2198: effect of welding parameters on fusion zone characteristics associated with mechanical properties

Experimental Study on Pores in Laser Welding of Magnesium Alloys

Microstructural, Porosity and Mechanical Properties of Lap Joint Laser Welding for 5182 and 6061 Dissimilar Aluminum Alloys under Different Place Configurations