Abstract:Fly ash has been widely explored in alkali-activated concrete technology as a precursor; however, it suffers sudden brittle failure and requires heat activation for early-strength development. Previous studies have demonstrated that these shortcomings can be overcome by adding nanosilica and various types of fibers. However, they were mainly focused on improving the mechanical properties, but there is no clear understanding of the durability and microstructural changes. Therefore, this study systematically addresses the effects of nanosilica sol and hybrid fibers (steel and polypropylene fibers) on the workability, porosity, flexural/ compressive strength development, flexural toughness, crack resistance, and durability (subjected to sulfuric acid of pH = 1, 5% sodium sulfate, and 3.5% seawater attacks) of fly ash-based mortars cured at ambient environments. The results demonstrate that nanosilica and hybrid fibers have acceptable simultaneous effects on the properties of mortar. Although they both reduce fluidity, nanosilica improves the pore enlargement caused by fiber materials; thus, it greatly improves the mechanical properties of mortar. The flexural toughness of the mortar with nanosilica and hybrid fibers was approximately 200% higher than that of the pure-fly ash. Only approximately 58.25 mm2 microcracks were observed during the early crack detection, and the residual strength also improved under chemical solution attack. The microstructures were studied by field-emission scanning electron microscopy with energy-dispersive X-ray spectroscopy, X-ray diffraction/Rietveld method, and nanoscale 3D X-ray microscopy. The nanosilica enhanced the reactivity of the precursors and refined the pore structure of the mortar due to the changes in the crystalline and amorphous phases, and the hybrid fibers produced composites with good internal characteristics and strong fiber/matrix interfacial bonding.

Study on Preparation of Mineral Polymer from Fly Ash

Preparation and Research of Fly Ash Based Mineral Polymer

Advance on Fly Ash-Based Mineral Polymer Material

Synthesis and Properties of Fly Ash Geopolymer with Dyeing Sludge

Research on Resource Utilization of Dyeing Sludge with High Calcium Fly Ash

Preparation of High-strength Mineral Polymer Based on Flyash:An Experimental Study

Study on Preparation of Quartz-Based Mineral Polymer by Autoclaved Process

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Study on the Geopolymer Based on Fly Ash and Slag

Preparation and properties of geopolymer containing phosphoric acid-activated fly ash and mechanically-milled kaolinite: Experiments and density function theory

Mechanism of Polymerization During the Solidification of Flyash-based Geopolymers

Preparation of Fly Ash-based Lightweight Loadbearing Wall Materials: an Experimental Study

Properties of geopolymer based on fly ash

Strength and microstructure of class C fly ash based geopolymer activated with sodium silicate powder

Preparation and Characterization of Functional Geopolymer

Study of Manufacture Process and Properties of Fly Ash-Based Geopolymers

Development of Low-Calcium Fly Ash-Based Geopolymer Mortar Using Nanosilica and Hybrid Fibers

Mechanical behavior and microstructure evolution of slag-fly ash based geopolymer stabilized sand

Study on Solidification of Cr3+ by Metakaolin-Fly Ash Based Geopolymer

An efficient approach for sustainable fly ash geopolymer by coupled activation of wet-milling mechanical force and calcium hydroxide

Realization of high-percentage addition of fly ash in the materials for the preparation of geopolymer derived from acid-activated metakaolin