Abstract:SiC/SiC composites, prepared by reactive melt infiltration (RMI), exhibit exceptional properties. However, the presence of residual Si in the composite matrix can significantly compromise their high-temperature mechanical properties. Addressing the issue of high-content residual Si aggregation remains a crucial focus of research in order to fully unlock the application potential of SiC/SiC composites prepared by RMI. In this work, a special porous carbon (C g ) is successfully synthesized and introduced into the porous 2D SiC/SiC composites prepared by CVI. The unique pore structure of the SiC/SiC-C g is thoroughly analyzed, along with its liquid Si infiltration process. The difference in coefficient of thermal expansion (CTE) between SiC and C g can cause thermal stress, which can destory the C g structure. Consequently, the C particles detach from the C g skeleton and react with liquid Si to create SiC. This process effectively separates residual Si and helps alleviate the negative effects of residual Si aggregation. The microstructure and phase distribution of SiC/SiC composites obtained by liquid Si infiltrating different C structures are investigated and compared, and it demonstrates the positive effect of C g on the uniform phase distribution of matrix in the composites. The as-received SiC/SiC composites possess a density of 2.94 g/cm 3 with open porosity of 1.23%, and a flexural strength of 808.7±10.2MPa, a fracture toughness of 25.5±1.8MPa·m 1/2 , a tensile strength of 317.4±12.4MPa and a proportional ultimate stress of 157.33±4.1MPa. Acoustic emission (AE) and digital image correlation (DIC) technology are used to study the special mechanical behavior of composites.

Structure and Properties of C/C-SiC Prepared by Reactive Melt Infiltration

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Mechanical and tribological properties of C/C–SiC ceramic composites with different preforms

Investigation of Impact of C/Si Ratio on the Friction and Wear Behavior of Si/SiC Coatings Prepared on C/C-SiC Composites by Slurry Reaction Sintering and Chemical Vapor Infiltration

Microstructures and properties of C/C–SiC composites derived from different gaseous carbon matrix precursors

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Effects of carbon content on microstructure and mechanical properties of SiC ceramics fabricated by SLS/RMI composite process

High strength C/Si‒Ni‒C composites fabricated by reaction melt infiltration with Si‒Ni alloy at lower temperature

Effect of SiC content on the mechanical behaviour of a three-dimensional needled C/SiC composite

Microstructure and flexural strength of C/HfC-ZrC-SiC composites prepared by reactive melt infiltration method

Microstructure and mechanical properties of SiC fiber/Si-CoSi2 matrix composites fabricated by carbon chemical vapor infiltration and Si alloy melt infiltration process

Microstructure and Mechanical Properties of Cf/SiC Composites with Dispersed C-SiC Interphase Prepared by Chemical Vapor Infiltration

Structural characterization and reaction mechanism of the Ti/SiC gradient material with Mg 2 Si additive fabricated by reaction sintering

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Bending and Thermal Expansion Properties of 2.5D C/SiC Composites

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation

Microstructure and mechanical properties of short-carbon-fiber/Ti3SiC2 composites

Microstructure of C/SiC Braking Material