Abstract:AlN-SiC multiphase ceramics possess robust mechanical strength, high thermal conductivity and good oxidization resistance, and show great potential as the matrix material of fiber reinforced ceramic matrix composites. In this work, AlN-SiC multiphase ceramics were fabricated via low temperature reactive melt infiltration of Si-Al alloy into porous C-Si3N4 preforms. Influence of Si-Al source on the melt infiltration process was studied, and impact of residual silicon on the mechanical and thermal properties of the AlN-SiC ceramics was investigated. It was found that an Al-O layer was in- situ formed at the interface between Si-Al melt and C-Si3N4 preform, when Si-Al powder was used as the infiltration medium. This seriously retarded the melt infiltration process and made the penetration of Si- Al melt into the C-Si3N4 preform hardly possible. However, when Si-Al ingot was used as the infiltration medium, a well infiltration of Si-Al melt into the C-Si3N4 preform occurred, which led to the formation of dense AlN-SiC ceramics. Mechanical and thermal property measurements indicated that the strength of the AlN-SiC ceramics was significantly improved as the residual silicon content in it was reduced, while a reverse trend was observed for the thermal conductivity. AlN-SiC ceramics with 4%( in mass) residual silicon showed a high strength of 320.1 MPa, nearly comparable to that of conventional reaction bonded SiC, although its thermal conductivity was modest (26.3 W center dot m(-1)center dot K-1). The fundamental reasons for the above phenomena were discussed. This study is of great significance for the preparation of SiCf/AlN-SiC composites by low temperature reactive melt infiltration.

High strength C/Si‒Ni‒C composites fabricated by reaction melt infiltration with Si‒Ni alloy at lower temperature

Fabrication and Properties of AlN-SiC Multiphase Ceramics <i>via</i> Low Temperature Reactive Melt Infiltration

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Fabrication and Mechanical Properties of Si3N4/SiC Nanocompoisites under Pressureless Sintering.

Mechanical properties of SiC fiber/carbon/Si‐Co matrix composites processed using film boiling and melt infiltration

Densification and Mechanical Properties of Si3N4/SiC Nanocomposite Using Si-Nitrided Si3N4 Powder

Microstructure and mechanical behavior of carbon fiber reinforced carbon, silicon carbide, and copper alloy hybrid composite fabricated by Cu-Si alloy melt infiltration

Fabrication and properties of Cf/ZrC‐SiC‐based composites by an improved reactive melt infiltration

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Effect of infiltration time on the microstructure and mechanical properties of C/C-SiC composite prepared by Si‐Zr10 alloyed melt infiltration

Structure and Properties of C/C-SiC Prepared by Reactive Melt Infiltration

Sandwich-structured C/C-SiC Composites Fabricated by Electromagnetic-Coupling Chemical Vapor Infiltration

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Mechanical Properties of Ceramic–metal Composites by Pressure Infiltration of Metal into Porous Ceramics

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Si3N4-SiCpComposites Reinforced Byin SituCo-Catalyzed Generated Si3N4Nanofibers

Analysis of Tensile Strength and Microstructure of Ni–SiC Composites Prepared by Electroforming

Microstructure and mechanical properties of SiC fiber/Si-CoSi2 matrix composites fabricated by carbon chemical vapor infiltration and Si alloy melt infiltration process

Mechanical properties and high temperature failure mechanism of carbon fibers reinforced polysilazane-derived SiCN ceramic matrix composites via PIP process

Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C