Abstract:Si3N4/SiC composites containing 0-30 vol% SiC were fabricated by pressureless sintering and sinter-post-HIPing method using fine Si3N4 and nano-sized SiC powders. Specimens reached full density (>96% theoretical density (th. d.)) except the composites made by pressureless sintering which contained a small amount of sintering additives or a large amount of SiC. All composites with 10 mass% sintering additives reached full density (similar to 99% th. d.) by sinter-post-HIPing. The addition of SiC particles greatly influenced the grain morphology of the Si3N4 matrix. The average grain thickness, length and aspect ratio decreased with increasing SiC content because of grain boundary pinning by SiC particles. Also the mechanical properties were markedly dependent upon the fraction of SiC particle reinforcement, as well as matrix grain size and porosity. When the materials were pressureless sintered, the strength of the composite increased with SiC additions below 20 vol%. Further increase in the SIC content resulted in a corresponding decrease in strength. Maximum strength of 1150 MPa was attained at 20 vol% SiC addition. The increase in strength by addition of SiC is due to decrease of grain size of Si3N4 matrix grain size, and the decrease by further increase in SiC content is caused by porosity and SiC agglomerate. On the other hand, toughness decreased monotonically with SiC content. The strength of all samples was enhanced by sinter-post-HIPing without any change in fracture toughness. The strength of sintered samples with 10-15 vol% SiC increased by similar to 20% to 1260 MPa by post-HIPing. The increase in strength by post-HIPing was interpreted as being due to a decrease flaw size.

Si3N4-SiC ceramic nanocomposites

Fabrication and Mechanical Properties of Si3N4/SiC Nanocompoisites under Pressureless Sintering.

Densification and Mechanical Properties of Si3N4/SiC Nanocomposite Using Si-Nitrided Si3N4 Powder

SiC-nanoparticle-reinforced Si3N4 matrix composites

C0.3N0.7Ti-SiC Toughed Silicon Nitride Hybrids with Non-Oxide Additives Ti3SiC2.

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics

Microstructure and mechanical properties of ZrB2–SiC nanocomposite ceramic

Study on the mechanical properties, microstructure and oxidation resistance of Si3N4/Si3N4W/Ti(C7N3) nanocomposites ceramic tool materials

Fabrication and mechanical properties of nano-/micro-sized Al2O3/SiC composites

Microstructures Andmechanical Properties of Hot-Pressed MoSi 2-Matrix Composites Reinforced with SiC and Si 3 N 4 Particles

Microstructure and Mechanical Properties of SiC/MoSi_2 Nanocomposites

Influence of SiCnp Content on the Microstructure and Mechanical Properties of ZrB2–SiC Nanocomposite

Influence of nanosized SiC particle on the fracture toughness of ZrB2-based nanocomposite ceramic

Fabrication and Mechanical Properties of SiC Reinforced Reaction-Bonded Silicon Nitride Based Ceramics

Fabrication and Mechanical Properties of Si3n4/Sic Nanocomposite with Pressureless Sintering and Sinter-Post-Hiping

Preparation and Properties for (SiC)Cf/Si3 N4 Composite

Effect of SiC content on properties of reaction sintered SiC-Si3N4 composites

Study of the mechanical properties, toughening and strengthening mechanisms of Si3N4/Si3N4w/TiN nanocomposite ceramic tool materials

Microstructure and mechanical properties of SiCp/MoSi2 composites prepared by in situ synthesis and hot-pressing

Mechanical Properties of NanoSiC Reinforced ZrB<sub>2</sub>-Based Ceramic Composite

Microstructure And Mechanical Properties Of Sic Ceramic Toughened With Tin Nanoparticles