Abstract:Low-temperature foaming is essential for the preparation of aluminum foam sandwich (AFS) using the powder metallurgy method. It ensures that the AFS panels, which are made of aluminum alloy plates, are not melted when the core layer is foamed. Therefore, the core material for the AFS should be an alloy with a low melting temperature, and it exhibits a better cellular structure and improved mechanical properties after foaming. In this study, foaming experiments were performed on Al-Si-Mg alloys at low temperature (<= 600 degrees C) and the effect of Cu and Sn addition to the cellular structure of aluminum foams was analyzed. The results show that alloys composed of Al, Mg and Si benefit from the addition of Sn and Cu by reducing the pore size and foaming temperature, respectively. In particular, the observed cellular structure with uniform pore size could be the result of the needle intermetallic phase Al2Cu formation in the cell wall. This intermetallic phase possible stabilized the bubble pores when Cu and Sn were added together. However, cracks were detected in the cell wall. They gradually increased and expanded with increasing Si content in the alloy, thus reducing the quasi-static axial compression strength of the aluminum foam. Furthermore, it was more difficult for the foamable precursor to achieve compaction when the Si content was increased to 10 wt%. The findings of the study show that AlMg4Si6Cu4Sn4 has better cellular structure and mechanical properties after foaming at 600 degrees C for 15 min.

Fabrication of Cu-Mg alloy foam with close pore structure by gas release reaction powder metallurgical approach

Fabrication of Mg-Al Alloy Foam with Close-Cell Structure by Powder Metallurgy Approach and Its Mechanical Properties

Fabrication of Cellular Zn–Mg Alloy Foam by Gas Release Reaction Via Powder Metallurgical Approach

Preparation principle and compression properties of cellular Mg–Al–Zn alloy foams fabricated by the gas release reaction powder metallurgy approach

Fabrication of Zn Alloy Foam Via Powder Metallurgical Approach

Fabrication of Cellular Mg Alloy by Gas Release Reaction Via Powder Metallurgical Approach

Low-Temperature Reactive Sintered Porous Mg-Al-Zn Alloy Foams

Factors affecting the microstructure of a fine ceramic foam

Reactive sintering principle and compressive properties of porous AZ91 magnesium alloy foams produced by powder metallurgy approach

Low-Temperature Fabrication of Porous Mg-Zn Foams by a Reactive Sintering Powder Metallurgy Approach

Fabrication of Al Foam Without Thickening Process Through Melt-Foaming Method

Effect of Cu and Sn Additions on the Cellular Structure of Al–Si–Mg Alloys Foaming at Low Temperature (≤600 °C)

Optimization of Mg Blowing Agent Content for Foaming Aluminum

Fabrication of Aluminum Foams with Small Pore Size by Melt Foaming Method

Effect of Grain Size on the Mechanical Properties of Mg Foams

Foamability and mechanical properties of in situ submicron MgAl2O4p/Al composite foams by ultrasonic method

Optimizing Calcium Addition for Fabricating Aluminum Foams with Different Pore Sizes

Production, stability and properties of ultrafine MgAl 2 O 4 (spinel) particles stabilized Mg–3Ca alloy foams

Mg-matrix syntactic foam filled with alumina hollow spheres coated by MgO synthesized with solution coating-sintering

Effect of Mg Powder’s Particle Size on Structure and Mechanical Properties of Ti Foam Synthesized by Space Holder Technique