Abstract:Synthesis of nanocomposites is challenging due to the difficulties in achieving homogeneous distribution of reinforcing particles in metal. In this paper, an in‐situ Al‐MgAl2O4 nanocomposite billet was prepared by the reaction of ɣ‐Al2O3 with molten Al and ultrasonication‐assisted impeller mixing. The microstructure of the composite showed homogeneously distributed MgAl2O4 crystals alongside their clusters in the Al matrix. Microstructural analysis revealed MgAl2O4 crystals distributed from 20 nm to 4 μm in size. The hardness was found to vary within the composite from 50 Hv for the matrix to 140 Hv for particle cluster regions. The grain size was reduced from 1000 μm in reference metal (CP Al) to 100 μm in the composite. The compression strength of the composite was increased substantially and higher strain hardening effect in comparison with Al was noticed in the compression test. The signatures of extensive plastic deformation such as dislocation pileups, deformed grains, grain boundary pinning etc. were observed in the composite via transmission electron microscopy. Damping properties of as‐cast composite were higher than those of CP Al in the temperature range from room temperature to 350 °C. After rolling the composite up to 40% reduction, the damping capacity (Tanδ) of the composite was found to increase marginally after 150 °C. Higher damping was found to reoccur after the annealing treatment of the composite. The improvement in damping capacity at RT was possibly influenced by the micron sized MgAl2O4 and at higher temperatures by the nano‐sized MgAl2O4 crystals. The reoccurrence of higher damping in the annealed composite underlined the stability of finer grains due to the grain boundary pinning by nano‐sized MgAl2O4 crystals. The studies on the damping property of the composite displayed the benefits of having dual size distribution of MgAl2O4 crystals (nm and μm) in the composite. This article is protected by copyright. All rights reserved.

Production, stability and properties of ultrafine MgAl 2 O 4 (spinel) particles stabilized Mg–3Ca alloy foams

Investigation on the stabilization behaviour of MgAl 2 O 4 (spinel) particles in aluminium foam via in-situ X-ray radioscopy and FIB tomography

Optimization of Mg Blowing Agent Content for Foaming Aluminum

Fabrication of Mg-Al Alloy Foam with Close-Cell Structure by Powder Metallurgy Approach and Its Mechanical Properties

Foamability and mechanical properties of in situ submicron MgAl2O4p/Al composite foams by ultrasonic method

Effect of Magnesium Addition on the Cell Structure of Foams Produced From Re-melted Aluminum Alloy Scrap

Pure Mg foams stabilized by CaO particles

Low-Temperature Reactive Sintered Porous Mg-Al-Zn Alloy Foams

Preparation and characterization of SiO2–Al2O3–MgO–CaO–based ceramic foams mainly from Ca–Mg–rich molybdenum tailings

Fabrication of Cu-Mg alloy foam with close pore structure by gas release reaction powder metallurgical approach

Fabrication of Al Foam Without Thickening Process Through Melt-Foaming Method

Study on an Aluminum Foam by Gas Injection Foaming

Preparation principle and compression properties of cellular Mg–Al–Zn alloy foams fabricated by the gas release reaction powder metallurgy approach

Effect of Aluminium Content and Processing Parameters on the Microstructure and Mechanical Properties of Laser Powder-Bed Fused Magnesium-Aluminium (0, 3, 6, 9wt%) Powder Mixture

Effect of Cu and Sn Additions on the Cellular Structure of Al–Si–Mg Alloys Foaming at Low Temperature (≤600 °C)

Synthesis and Characterisation of Floatable Magnesium Alloy Syntactic Foams with Hybridised Cell Morphology

Reactive sintering principle and compressive properties of porous AZ91 magnesium alloy foams produced by powder metallurgy approach

Effect of alumina sol on the preparation of magnesia‐alumina spinel foam ceramics by foaming‐sol method

Microstructural evolution and property evaluation of in‐situ Al‐MgAl2O4 nanocomposite prepared by ɣ‐Al2O3 and ultrasonication‐assisted impeller mixing

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Investigation on the Structural and Mechanical Properties of Al Foam Manufactured by Spark Plasma Sintering and Compression Molding Methods